This chapter describes how notches affect the load-carrying capacity and fatigue life of materials under cyclic loads. It explains that stresses and strains can be three to four times higher in the vicinity of a notch, greatly accelerating fatigue damage. It discusses the use of stress concentration factors and how they are determined for the general case and for specific geometries, materials, and surface conditions. The chapter covers both elastic and plastic fatigue behaviors as well as a wide range of methods. It also explains how small nuances in loading can introduce tensile or compressive stress in the hysteresis loops causing variations in fatigue life as large as 50:1 depending on where the transition in fatigue behavior occurs.

This article focuses on characterization techniques used for analyzing the physical behavior and chemical composition of thermoset resins, namely chromatography and infrared spectroscopy. The main purpose is to give sufficient detail to permit the reader understand a particular test technique and its value to the thermoset resin field. Epoxy resins are emphasized in the examples because they dominate the airframe and aerospace industries. The article also provides information on two categories of characterization of the processing behavior of thermoset. The first studies the thermal properties of reactive thermoset systems, while the second utilizes these thermal characteristics as the basis for monitoring and control during processing.

Powder metallurgy plays a central role in the production of nearly all beryllium components. This chapter describes the primary steps in the powder metal process and the work that has been done to improve each one. It explains how beryllium powders are made and how they are consolidated prior to sintering. It also compares and contrasts the properties of beryllium products made using different methods and provides composition and particle size data on commercially available powders.

This chapter provides information and data on the fatigue and fracture properties of steel, aluminum, and titanium alloys. It explains how microstructure, grain size, inclusions, and other factors affect the fracture toughness and fatigue life of these materials and the extent to which they can be optimized. It also discusses the effect of metalworking and heat treatment, the influence of loading and operating conditions, and factors such as corrosion damage that can accelerate crack growth rates.

The crux of this chapter is to develop a method to quantitatively define hardenability. The chapter includes the empirical methods to estimate the hardenability knowing the chemical composition, describes prior austenite grain size, and examines their utility. It then reviews the Jominy end-quench test and explains its relation to hardenability. The chapter outlines the concepts of the critical diameter and the ideal critical diameter, leading to establishing a quantitative measure of hardenability. Next, it examines methods that have been developed which allow estimation of the ideal critical diameter from the chemical composition and the austenite grain size. The chapter reviews the methods which allow calculation of the Jominy curve from a value of the ideal critical diameter. Additionally, it describes the selection and application of H-band steels. Finally, the chapter describes the effect of boron on the hardenability of steels.

This chapter addresses the challenge of selecting an appropriate stress-corrosion cracking (SCC) test to evaluate the serviceability of a material for a given application. It begins by establishing a generic model in which SCC is depicted in two stages, initiation and propagation, that further subdivide into several zones plus a transition region. It then discusses SCC test standards before describing basic test objectives and selection criteria. The chapter explains how to achieve the required loading conditions for different tests and how to prepare test specimens to determine elastic strain, plastic strain, and residual stress responses. It also describes the difference between smooth and precracked specimens and how they are used, provides information on slow-strain-rate testing and how to assess the results, and discusses various test environments and procedures, including tests for weldments. The chapter concludes with a section on how to interpret time to failure, threshold stress, percent survival, stress intensity, and propagation rate data, and assess the precision of the associated tests.

Compared with other deformation processes used to produce semifinished products, the hot-working extrusion process has the advantage of applying pure compressive forces in all three force directions, enhancing workability. The available variations in the extrusion process enable a wide spectrum of materials to be extruded. This chapter focuses on the processes involved in the extrusion of semifinished products in various metals and their alloys, namely tin, lead, lead-base soft solders, tin-base soft solders, zinc, magnesium, aluminum, copper, titanium, zirconium, iron, nickel, and powder metals. It discusses their properties and applications as well as suitable equipment for extrusion. It further discusses the processes involved in the extrusion of semifinished products in exotic alloys and extrusion of semifinished products from metallic composite materials.