This chapter outlines the step-by-step processes by which materials are selected in order to prevent or control corrosion and includes information on materials that are resistant to the various forms of corrosion. The various forms of corrosion covered are general (uniform) corrosion, localized corrosion, galvanic corrosion, intergranular corrosion, stress-corrosion cracking, hydrogen damage, and erosion-corrosion. In addition, the economic importance of cost-effective materials selection is also considered.

The design process is the first and most important step in corrosion control. Major savings in operating costs are possible by anticipating corrosion problems so as to provide proper design for equipment before assembly or construction begins. This chapter describes the role of the design team in producing a successful final design, general considerations in corrosion-control design, and design details that accelerate corrosion. The details that must be considered when attempting to control corrosion by design include plant/site location, plant environment, component/assembly shape, fluid movement, surface preparation and coating procedures, and compatibility, insulation, and stress considerations. Design solutions for specific forms of corrosion, namely crevice corrosion, galvanic corrosion, erosion-corrosion, and stress-corrosion cracking, are then considered. A brief section is devoted to the discussion on corrosion allowance used for steel parts subject to uniform corrosion. Finally, the chapter describes the design considerations for using weathering steels.

The challenge of materials selection is to achieve adequate performance at the lowest possible cost. Corrosion resistance is not the only property to be considered in making materials selections. Typical requirements and some of the procedures involved in making a selection and some of the factors that must be considered when determining the corrosion performance of a given material are listed in this chapter. The various steps that might be included in a materials selection process are then examined. These include a review of operating conditions and design, the selection of candidate materials, the in-depth evaluation of each candidate material, fabrication requirements, follow-up monitoring, and final materials selection. Material considerations such as cost, materials properties, and processing and fabrication requirements are subsequently covered. Finally, the chapter provides information on materials selection under general corrosion conditions and under conditions of localized corrosion forms such as pitting, crevice corrosion, and stress-corrosion cracking.

Organic coatings (paints and plastic or rubber linings), metallic coatings, and nonmetallic inorganic coatings (conversion coatings, cements, ceramics, and glasses) are used in applications requiring corrosion protection. These coatings and linings may protect substrates by three basic mechanisms: barrier protection, chemical inhibition, and galvanic (sacrificial) protection. This chapter begins with a section on organic coating and linings, providing a detailed account of the steps involved in the coating process, namely, design and selection, surface preparation, application, and inspection and quality assurance. The next section discusses the methods by which metals, and in some cases their alloys, can be applied to almost all other metals and alloys: electroplating, electroless plating, hot dipping, thermal spraying, cladding, pack cementation, vapor deposition, ion implantation, and laser processing. The last section focuses on nonmetallic inorganic coatings including ceramic coating materials, conversion coatings, and anodized coatings.

This article describes in detail the process of corrosion control by cathodic and anodic protection. The discussion covers the basic concept of cathodic and anodic protection systems, their types and equipment used, and the advantages, limitations, and applications of these protection systems. The types of cathodic protection systems include sacrificial cathodic protection and impressed-current cathodic protection systems. Some of the technical problems associated with cathodic protection include the effects of stray currents on the corrosion of adjacent metal structures, the effects of the chemical reactions occurring at the surface of the protected structure, and the effects of cathodic protection on coatings.

Corrosion can be defined as a chemical or electrochemical reaction between a material, usually a metal, and its environment that produces a deterioration of the material and its properties. This chapter describes the effects and economic impact of corrosion in major industrial plants. The emphasis in this chapter, as well as in other chapters in this book, is on aqueous corrosion, or corrosion in environments where water is present. The chapter describes the classification of various forms of corrosion based on the nature of the corrodent, mechanism of corrosion, and appearance of the corroded metal. It discusses five primary methods of corrosion control, namely, material selection, coatings, inhibitors, cathodic protection, and design. Examples of the opportunities in corrosion control and the means to implement a program to capitalize on those opportunities are presented in a table. The chapter concludes with varied sources of information pertaining to corrosion and corrosion prevention.

Anodic protection is used on a smaller scale than other corrosion control techniques due to the fundamental electrochemistry involved. This chapter provides a brief history of the technique, discusses anodic protection use, and compares anodic and cathodic protection. The background and theory of anodic protection are summarized. In addition to briefly describing the various items used for each component of an anodic protection system, the chapter presents design concerns as well as applications of the system. Factors concerning the economic justification of anodic protection are also described.

This chapter discusses the particular corrosion problems encountered and the methods of control used in petroleum production and the storage and transportation of oil and gas up to the refinery. It begins by describing those aspects of corrosion that tend to be unique to corrosion as encountered in applications involving oil and gas exploration and production. This is followed by a section reviewing the methods of corrosion control, namely the proper selection of materials, protective coatings, cathodic protection systems, use of inhibitors, use of nonmetallic materials, and control of the environment. The chapter ends with a discussion on the problems encountered and protective measures that are based on the state-of-the-art as practiced daily by corrosion and petroleum engineers and production personnel.

This chapter presents the primary considerations and mechanisms for corrosion and how they are involved in the selection of materials for process equipment in petroleum refineries and petrochemical plants. In addition, specific information on mechanical properties, corrosion, sulfide stress cracking, hydrogen-induced cracking, stress-oriented hydrogen-induced cracking, hydrogen embrittlement cracking, stress-corrosion cracking, velocity-accelerated corrosion, erosion-corrosion, and corrosion control is provided.

This chapter provides a detailed account of cathodic protection. It begins by discussing the fundamentals of cathodic protection followed by a description of the various types of cathodic protection. It then describes the origins, types, and alleged failures of cathodic protection criteria. This is followed by a section providing information on anode materials that are used for cathodic protection applications. General guidelines for designing the cathodic protection systems are also listed. Finally, the chapter presents various examples on cathodic protection of steel structures. The examples are selected to familiarize the design engineer with the steps to follow in selecting a specific corrosion-control method.

This chapter first covers some basic principles of electrochemical corrosion and then some of the various types of corrosion. Some of the more common types of corrosion discussed include uniform corrosion, galvanic corrosion, pitting, crevice corrosion, erosion-corrosion, cavitation, fretting corrosion, intergranular corrosion, exfoliation, dealloying corrosion, stress-corrosion cracking, and corrosion fatigue. The chapter discusses the processes involved in corrosion control by retarding either the anodic or cathodic reactions. The rate of corrosion is reduced by conditioning of the metal, by conditioning the environment, and by electrochemical control. Finally, the chapter deals with high-temperature oxidation that usually occurs in the absence of moisture.

This chapter focuses on various factors to be considered at design stage to minimize corrosion. It begins by providing information on design considerations and general corrosion awareness. This is followed by a description of several factors influencing materials-component failure. Details on design and materials selection, which assist in controlling corrosion, are then provided. The chapter ends with a discussion on the design factors that influence corrosion.

This chapter provides a detailed account of corrosion inhibitors for oil and gas production. It begins by discussing some of the demands of competitive industry on inhibitor formulations. It then describes the varying characteristics of oil wells, gas wells, water injection systems, and pipelines. The following sections provide information on the factors influencing corrosivity of produced fluids and the methods of inhibitor application. The chapter discusses the primary causes of corrosion problems and inhibition in waterfloods and provides an overview of bacteria-induced corrosion. Various laboratory testing methods of corrosion inhibitors and the methods used to monitor corrosion rates and inhibitor effectiveness are also presented. The chapter ends by providing information on quality control of inhibitors and computerization of inhibitor treating programs.

This chapter discusses the formation and control of aqueous corrosion in iron and steel. It also provides information on passivation, stress corrosion, rust, and direct oxidation.

This chapter focuses on the effects of microscopic organisms and the by-products they produce on the electrochemical corrosion of metals. It begins by considering the characteristics of organisms that allow them to interact with the corrosion processes, the mechanisms by which organisms can influence the occurrence or rate of corrosion, and the types of corrosion most often influenced by microbes. The chapter then discusses the formation of biofilms on the surface of metals. This is followed by a list of industries most often reported as being affected by microbiological corrosion, along with the organisms usually implicated in the attack. The types of attack that have most commonly been documented are illustrated through generalized case histories for different classes of alloys. The chapter also describes the general approaches to be taken to prevent microbiologically influenced corrosion. It ends with some information on the inhibition of corrosion by the action of bacteria.

This chapter examines methods of internal corrosion prediction for multiphase pipelines and details methodologies to perform internal corrosion direct assessment for natural gas pipelines. Further, real-time monitoring techniques for assessing actual corrosion at critical locations are discussed.

Corrosion testing and monitoring are powerful tools in the fight to control corrosion. This chapter provides a general overview of three major categories of corrosion tests, namely laboratory tests, pilot-plant tests, and field tests. It begins with brief sections describing the purposes of corrosion tests, the logical steps in a test program, and the preparation and cleaning of test specimens. The focus then moves on to discuss the types and applications of these test categories and the associated evaluation procedures. Excluding electrochemical tests which are addressed separately in this chapter, the other laboratory tests covered under this category are simulated atmosphere tests, salt-spray tests, and immersion tests. Only corrosion testing in the atmosphere is discussed in the section on field tests. Corrosion monitoring techniques are finally considered, covering the characteristics of corrosion monitoring techniques, the factors to be considered in selecting a corrosion-monitoring method, and the strategies in corrosion monitoring.

This chapter discusses the principles of corrosion of metals in aqueous environments. The thermodynamics of aqueous corrosion is the subject of the first half of this chapter, which addresses concepts such as corrosion reactions and free-energy change, the relationship between free energy and electrochemical potential, the effect of ionic concentration on electrode potential, and the corrosion behavior of a metal based on its potential-pH diagram. The corrosion (potential-pH) behavior of iron, gold, copper, zinc, aluminum, and titanium are described. Understanding the kinetics of corrosion and the factors that control the rates of corrosion reactions requires examination of the concepts of polarization behavior and identification of the various forms of polarization in an electrochemical cell. These concepts, addressed in the remaining of this chapter, include anodic and cathodic reactions, the mixed-potential theory, and the exchange currents.