Fig. 12 Pitting of underalloyed (relative to base metal) type 308L weld metal. The type 316L stainless steel base metal is unaffected. About 2.5× More

Fig. 20 Chloride SCC of type 304 stainless steel base metal and type 308 weld metal in an aqueous chloride environment at 95 °C (200 °F). Cracks are branching and transgranular. More

Fig. 9 Pitting corrosion resistance of base metal relative to weld metal placed in 6 wt % FeCl 3 solution for 24 h duration per ASTM 648 (method A). Source: Ref 14 More

Fig. 9 Pitting of underalloyed (relative to the base metal) type 308L weld metal. The type 316L stainless steel base metal is unaffected. About 2.5× More

Fig. 22 Pitting corrosion resistance of base metal relative to weld metal placed in 6 wt% FeCI 3 solution for 24 h per ASTM G 48 (method A). Source: Ref 35 More

Fig. 40 Energy-dispersive x-ray spectroscopy spectra of (a) the base metal of the screw and (b) the plating on the outside surface. Source: Ref 20 More