This chapter covers the failure modes and mechanisms associated with boiler components and the tools and techniques used to assess damages and predict remaining component life. It begins with a review of the design and operation of a utility boiler and the materials used in construction. It then describes the various causes of failure in boiler tubes, headers, and steam pipes, explaining how and why they occur, how they are diagnosed, and how to mitigate their effects. The final and by far largest section in the chapter is a tutorial on damage and life assessment techniques for boiler components and assemblies. It demonstrates the use of various methods, including analytical techniques that estimate life expenditure based on operating history, component geometry, and material properties; predictive methods based on the extrapolation of failure statistics; methods that predict life based on dimensional measurements; methods based on metallographic studies; methods based on temperature estimates; and a method for estimating remaining life under creep conditions based on stress-rupture testing of service-exposed material samples. The chapter also discusses the use of fracture mechanics and presents a number of cases in which life assessments are made based on the integration of several methods.

Increasing the efficiency of power plants by operating at higher temperatures and pressures and adding a double-reheat feature comes at the expense of shortened lifetimes for critical components. This chapter provides an overview of the material-related problems associated with advanced steam plants and their respective solutions. The discussion covers the selection of materials on a component-specific basis for boilers as well as steam turbines.

Boilers are often classified based on the maximum operating temperature and pressure for which they are designed. Classifications, in ascending order, are subcritical, supercritical, ultra-supercritical, and to advanced ultra-supercritical. At each higher operating point comes greater efficiency, as well as greater demand on construction materials. This chapter discusses the primary requirements for boiler tube materials, including oxidation and corrosion resistance, fatigue strength, thermal conductivity, and the ability to resist creep and rupture. It also provides information on various steels and alloys, covering cost, engineering specifications, and ease of use.

The ability to accurately assess the remaining life of components is essential to the operation of plants and equipment, particularly those in service beyond their design life. This, in turn, requires a knowledge of material failure modes and a proficiency for predicting the near and long term effects of mechanical, chemical, and thermal stressors. This chapter presents a broad overview of the types of damage to which materials are exposed at high temperatures and the approaches used to estimate remaining service life. It explains how operating conditions in power plants and oil refineries can cause material-related problems such as embrittlement, creep, thermal fatigue, hot corrosion, and oxidation. It also discusses the factors and considerations involved in determining design life, defining failure criteria, and implementing remaining-life-assessment procedures.

Coal-based thermal power plants play a major role in the welfare of many nations and the overall global economy. This chapter describes the basic equipment requirements and operating principles of thermal power plants, particularly subcritical, supercritical, and ultra-supercritical types.

This chapter describes nondestructive evaluation (NDE) test methods and their relative effectiveness for diagnosing the cause of stress-corrosion cracking (SCC) service failures. It discusses procedures for analyzing various types of damage in carbon and low-alloy steels, high-strength low-alloy steels, hardenable stainless steels, austenitic stainless steels, copper-base alloys, titanium and titanium alloys, aluminum and aluminum alloys, and nickel and nickel alloys. It identifies material-environment combinations where SCC is known to occur, provides guidelines on how to characterize cracking and fracture damage, and explains what to look for during macroscopic and microscopic examinations as well as chemical and metallographic analyses. It also includes nearly a dozen case studies investigating SCC failures in various materials.

Boilers are engineered systems designed to convert the chemical energy in fuel into heat to generate hot water or steam. This chapter describes boiler applications and types, including firetube boilers, watertube boilers, electric boilers, packaged boilers, fluidized bed combustion boilers, oil- and gas-fired boilers, waste heat boilers, and black liquor recovery boilers. It also describes the operation and working principle of utility or power plant boilers, covering conventional subcritical and advanced supercritical types.

Water chemistry is a factor in nearly all boiler tube failures. It contributes to the formation of scale, biofilms, and sludge, determines deposition rates, and drives the corrosion process. This chapter explains how water chemistry is managed in boilers and describes the effect of impurities and feedwater parameters on high-pressure boiler components. It discusses deposition and scaling, types of corrosion, and carryover, a condition that occurs when steam becomes contaminated with droplets of boiler water. The chapter also covers water treatment procedures, including filtration, chlorination, ion exchange, demineralization, reverse osmosis, caustic and chelant treatment, oxygen scavenging, and colloidal, carbonate, phosphate, and sodium aluminate conditioning.

This chapter discusses the effects of corrosion on boiler tube surfaces exposed to water and steam. It describes the process of corrosion, the formation of scale, and the oxides of iron from which it forms. It addresses the primary types of corrosion found in boiler environments, including general corrosion, under-deposit corrosion, microbially induced corrosion, flow-accelerated corrosion, stress-assisted corrosion, erosion-corrosion, cavitation, oxygen pitting, stress-corrosion cracking, and caustic embrittlement. The discussion is supported by several illustrations and relevant case studies.

This chapter reviews the development of filament winding systems and the automated processes used in state-of-the-art filament winding facilities. It first provides a description on the early stages of modern filament winding, followed by brief information on the advances of filament winding in the computer age. Then, the chapter discusses the requirements for filament winding in manufacturing oil and gas industry components and in high-volume production of sporting goods, propane tanks, and curing ovens. The chapter concludes with examples of the versatility of filament winding in producing complex parts.

Failure analysis of steel welds may be divided into three categories. They include failures due to design deficiencies, weld-related defects usually found during inspection, and failures in field service. This chapter emphasizes the failures due to various discontinuities in the steel weldment. These include poor workmanship, a variety of hydrogen-assisted cracking failures, stress-corrosion cracking, fatigue, and solidification cracking in steel welds. Hydrogen-assisted cracking can appear in four common forms, namely underbead or delayed cracking, weld metal fisheyes, ferrite vein cracking, and hydrogen-assisted reduced ductility.

Carbon and low-alloy steels in high-temperature service are vulnerable to the effects of hydrogen attack, which include severe loss in tensile and rupture strengths as well as ductility. As the chapter explains, when steel is in contact with hydrogen molecules at elevated temperatures, hydrogen atoms can be absorbed at the surface and then diffuse into the metal. Hydrogen atoms in the metal then react with iron carbide forming methane gas which can accumulate at grain boundaries and other interfaces. The chapter describes two applications, one in coal-fired boilers, the other in petroleum refining, where hydrogen attack was observed. It documents the extent of the damage in each case and identifies the source of the hydrogen.

This chapter presents the primary considerations and mechanisms for corrosion and how they are involved in the selection of materials for process equipment in petroleum refineries and petrochemical plants. In addition, specific information on mechanical properties, corrosion, sulfide stress cracking, hydrogen-induced cracking, stress-oriented hydrogen-induced cracking, hydrogen embrittlement cracking, stress-corrosion cracking, velocity-accelerated corrosion, erosion-corrosion, and corrosion control is provided.

This chapter examines the stress-corrosion cracking (SCC) failure of stainless steel pipe welds in boiling water reactor (BWR) service. It explains where most of the failures have occurred and provides relevant details about the materials of construction, fabrication techniques, environmental factors, and cracking characteristics. It includes a model that accounts for the primary factors involved in intergranular SCC, namely, tensile stresses above the yield stress of the base material, a sensitized microstructure, and reactor cooling water. The chapter also provides proven remedies and mitigation techniques corresponding to a wide range of issues related to stress, sensitization, and operating conditions.

Elevated-temperature failures are the most complex type of failure because all of the modes of failures can occur at elevated temperatures (with the obvious exception of low-temperature brittle fracture). Elevated-temperature problems are real concerns in industrial applications. The principal types of elevated-temperature failure mechanisms discussed in this chapter are creep, stress rupture, overheating failure, elevated-temperature fatigue, thermal fatigue, metallurgical instabilities, and environmentally induced failure. The causes, features, and effects of these failures are discussed. The cooling techniques for preventing elevated-temperature failures are also covered.

This chapter describes the origins of solders and soldering, covering the composition of solders and applications of soldering.

Boiler tubes subjected to cyclic or fluctuating loads over extended periods of time are prone to fatigue failure. Fatigue can occur at relatively low stresses and is implicated in almost 80% of the tube failures in firetube boilers. This chapter covers the most common forms of boiler tube fatigue, including mechanical or vibrational fatigue, corrosion fatigue, thermal fatigue, and creep-fatigue interaction. It discusses the causes, characteristics, and impacts of each type and provides several case studies.