Cross-sectioning refers to the process of exposing the internal layers and printed devices below the surface by cleaving through the wafer. This article discusses in detail the steps involved in common cross-sectioning methods. These include sample preparation, scribing, indenting, and cleaving. The article also provides information on options for mounting, handling, and cleaning of samples during and after the cleaving process. The general procedures, tools required, and considerations that need to be taken into account to perform these techniques are considered.

A high-pressure turbine blade in an aircraft engine failed prematurely, fracturing close to the root. Visual examination revealed significant plastic deformation on the leading edge of the blade, blocky cleavage on the trailing edge, and a region covered with fissures in between. Based on their observations and the results of SEM imaging described in the chapter, investigators concluded that the blade failed by low-cycle fatigue, acting on a preexisting crack.

A cardon shaft operating in an aircraft engine failed and was taken out and analyzed to determine the cause. A photograph of the broken shaft in the as-received condition shows the location and orientation of the fracture. The fracture surface appeared smooth, indicating that a considerable amount of rubbing occurred after the shaft broke. SEM fractography revealed deformation marks and elongated dimples, typical of shear overloads, along with other details. Based on their analysis, investigators concluded that the cardan shaft failed under torsional overload. They also cited a need for a more detailed examination of the driven end of the shaft.

The quill shaft in an aircraft engine was found in two pieces following a flameout. One piece was short, straight, and otherwise undamaged; the other piece was bent in several places as was the sleeve that covered it. The facture surface, as viewed under optical and scanning electron microscopes, was flat and shiny with deformation marks and dimples, typical of torsional overload, and signs of severe rubbing on the periphery. Based on their observations, investigators concluded that the quill shaft failed by torsional overload, the source of which could not be determined.

This article covers common techniques for surface characterization, including the modern scanning electron microscopy and methods for the chemical characterization of surfaces by Auger electron spectroscopy, X-ray photoelectron spectroscopy, and time-of-flight secondary ion mass spectrometry. The principles of surface analysis and some of the applications of the technique in polymer failure studies are also provided.

After the fault-tree, a failure-cause identification method has identified potential failure causes and the failure analysis team has prepared a failure mode assessment and assignment (FMA&A). The team knows specifically what to search for when examining components and subassemblies from the failed system. There are numerous techniques and technologies available for examining and analyzing components and subassemblies, which are categorized as follows: optical approaches, dimensional inspection and related approaches, nondestructive test approaches, mechanical and environmental approaches, and chemical and composition analysis for assessing material characteristics. This chapter is a detailed account of the working principle and the steps involved in these techniques and technologies.

An aircraft crashed following the loss of yaw control in full airborne flight. The subsequent discovery of broken shutter bolts in the rear pitch reaction control valve led to an inspection campaign that found bolt failures of a similar nature in valves on several other aircraft. The bolts were removed and analyzed to determine the mode and cause of failure. Based on the results of macroscopy, scanning electron fractography, metallographic examination, and chemical analysis, the failures were caused by stress corrosion cracking, and in one case, overtightening.

A turbine blade in an aircraft engine failed, fracturing at the root above the fir tree region. Fractography indicated that a fatigue crack initiated at the trailing edge of the blade and the final fracture occurred when the crack reached critical length. Although the exact cause of crack initiation could not be established, material defects, improper root loading, and high operating temperatures were ruled out. This chapter describes how investigators came to their conclusions and what they learned through visual and SEM examination and qualitative elemental analysis. It includes images of the microstructure and fracture surfaces and explains what some of the details reveal about the failure.

Two filtration components installed on a developmental aircraft cracked during pressure impulse testing. Both parts were made from an aluminum alloy, solutionized and aged, and cracked due to fatigue. In both cases, the crack initiated at a transition region on an inner surface and progressed circumferentially outward. Based on these observations and the results of SEM fractography and microstructural analysis, the fatigue cracking can be traced to insufficient fillet radius at the transition zone.

This chapter presents various case histories that illustrate a variety of failure mechanisms experienced by the high-strength steel components in aerospace applications. The components covered are catapult holdback bar, AISI 420 stainless steel roll pin, main landing gear (MLG) lever, inboard flap hinge bolt, nose landing gear piston axle, multiple-leg aircraft-handling sling, aircraft hoist sling, internal spur gear, and MLG axle. In addition, the chapter provides information on full-scale fatigue testing, nondestructive testing, and failure analysis of fin attach bolts.

This chapter provides an overview of the tools and techniques used to examine failure specimens and the wealth of information that can be obtained from fracture surfaces, cracks, wear patterns, and other such features. It discusses the use of metallography, fractography, and optical and electron microscopy. It presents a number of images recorded using these methods and explains what they reveal about the mode of fracture and the state of the component prior to failure.

Several specialized instruments are available for the metallographer to use as tools to gather key information on the characteristics of the microstructure being analyzed. These include microscopes that use electrons as a source of illumination instead of light and x-ray diffraction equipment. This chapter describes how these instruments can be used to gather important information about a microstructure. The instruments covered include image analyzers, transmission electron microscopes, scanning electron microscopes, electron probe microanalyzers, scanning transmission electron microscopes, x-ray diffractometers, microhardness testers, and hot microhardness testers. A list of other instruments that are usually located in a research laboratory or specialized testing laboratory is also provided.

An aircraft went down over water some 30 minutes into a flight. The wreckage was retrieved and the elevator linkage components were dismantled, cleaned, and reassembled. As the chapter explains, both the port and starboard hinge pins had fractured at a tack welded joint along a flange. Based on visual examination, SEM fractography, and chemical analysis, investigators concluded that the hinge pins were not made from the specified steel and were not properly treated after cadmium plating. The pins failed due to hydrogen embrittlement, which may have been aggravated by welding. The chapter provides several recommendations to avoid such failures in the future.

A pair of bolts on a connecting rod failed during a test run for a prototype engine. They were replaced by bolts made from a stronger material that also failed, one due to fatigue, the other by tensile overload. The fracture surfaces on all four bolts were examined using optical and electron microscopes, indicating that the operating loads on the bolts far exceeded the design loads. Based on their observations, which are summarized in the report, failure analysts concluded that the design of the connecting rod system needs to be reassessed.

A compressor blade made of titanium alloy fractured during an engine test. The material and processing conditions of the blade were found to be satisfactory, turning the focus of the investigation to operating anomalies and human error. A photograph of the failed blade shows well-defined chevron marks along the fracture surface that end in a shear lip on the convex side. Further examination using a SEM shows that the failure was due to overload. Based on these observations and the results of tensile testing and microstructural analysis, investigators concluded that a sudden impact load on the concave side of the blade caused it to fracture.