This chapter describes issues related to corrosion of carbon steel weldments and remedial measures that have proven successful in specific cases. The forms of corrosion covered includes preferential heat affected zone corrosion, preferential weld metal corrosion, and galvanic corrosion. Industrial case studies demonstrating the necessity for testing each galvanic couple in the environment for which it is intended are presented. The chapter also discusses various factors associated with stress-corrosion cracking in oil refineries.

This chapter describes various units and process streams that are often susceptible corrosion inhibitors in crude oil refineries, discusses the types and applications of corrosion inhibitors, and provides some information on corrosion monitoring techniques used at refineries.

This chapter discusses the particular corrosion problems encountered and the methods of control used in petroleum production and the storage and transportation of oil and gas up to the refinery. It begins by describing those aspects of corrosion that tend to be unique to corrosion as encountered in applications involving oil and gas exploration and production. This is followed by a section reviewing the methods of corrosion control, namely the proper selection of materials, protective coatings, cathodic protection systems, use of inhibitors, use of nonmetallic materials, and control of the environment. The chapter ends with a discussion on the problems encountered and protective measures that are based on the state-of-the-art as practiced daily by corrosion and petroleum engineers and production personnel.

This chapter presents the primary considerations and mechanisms for corrosion and how they are involved in the selection of materials for process equipment in petroleum refineries and petrochemical plants. In addition, specific information on mechanical properties, corrosion, sulfide stress cracking, hydrogen-induced cracking, stress-oriented hydrogen-induced cracking, hydrogen embrittlement cracking, stress-corrosion cracking, velocity-accelerated corrosion, erosion-corrosion, and corrosion control is provided.

This chapter discusses various factors pertinent to the prevention of corrosion in alloys for petroleum applications and reviews the selection of stainless steels for petroleum applications, including oil country tubular goods, line pipe, offshore platforms, liquefied natural gas vessels, and refinery equipment.

Fireside corrosion can be a serious problem in oil-fired boilers and in refinery furnaces fired with low-grade fuels. This chapter provides an overview of fireside or oil-ash corrosion and the problems it can cause in utility power boilers and petrochemical refinery furnaces. It explains how oil-ash corrosion affects waterwalls, superheaters, and reheaters as well as metal tube supports and hangers.

Carbon and low-alloy steels in high-temperature service are vulnerable to the effects of hydrogen attack, which include severe loss in tensile and rupture strengths as well as ductility. As the chapter explains, when steel is in contact with hydrogen molecules at elevated temperatures, hydrogen atoms can be absorbed at the surface and then diffuse into the metal. Hydrogen atoms in the metal then react with iron carbide forming methane gas which can accumulate at grain boundaries and other interfaces. The chapter describes two applications, one in coal-fired boilers, the other in petroleum refining, where hydrogen attack was observed. It documents the extent of the damage in each case and identifies the source of the hydrogen.

This chapter reviews weld corrosion in three key application areas: petroleum refining and petrochemical operations, boiling water reactor piping systems, and components used in pulp and paper plants. The discussion of each area addresses general design and service characteristics, types of weld corrosion issues, and prevention or mitigation strategies.