A tie rod on a 70-ton aircraft towing tractor failed during a test run, fracturing near a welded bracket that connects to a hydraulic jack. This chapter discusses the failure and the investigation that followed. It presents a close-up view of the fracture surface showing what appears to be a brittle fracture that initiated from a zone of poor-quality weld. It also provides photographic evidence of a weld crack in the heat-affected zone and includes a drawing of a modified weld design that passed subsequent testing.

During a routine preflight inspection of a piston aircraft engine, part of a cooling fin was found that had broken off the cylinder. The piece, made of aluminum-silicon alloy, was cleaned and examined. Based on the fracture characteristics revealed by an electron microscope, it was concluded that the fin failed in a brittle manner by overload.

A driven gear in the gear box of an aircraft engine fractured after a 40 h test run. The driving gear and gear shaft were also damaged. Based on the results of fractography, chemical analysis, metallography, and hardness testing, the fracture was caused by a fatigue crack initiating at the corner of the inner rim near an inclusion. The report recommends the use of a cleaner material and more carefully controlling case hardening process.

A pair of bolts on a connecting rod failed during a test run for a prototype engine. They were replaced by bolts made from a stronger material that also failed, one due to fatigue, the other by tensile overload. The fracture surfaces on all four bolts were examined using optical and electron microscopes, indicating that the operating loads on the bolts far exceeded the design loads. Based on their observations, which are summarized in the report, failure analysts concluded that the design of the connecting rod system needs to be reassessed.