Compacted graphite iron (GCI) is a cast iron grade that is engineered through graphite morphology modifications to achieve a combination of thermal and mechanical properties that are in between those of flake graphite iron and ductile iron. This chapter discusses the advantages of compacted graphite iron over gray iron and ductile iron. It presents examples of low- and high-frequency thermal cycling, both of which affect the thermal stresses that castings are exposed to during temperature fluctations. Information on optimum carbon and silicon ranges as well as mechanical property standards for CGI are provided. The chapter describes the critical factors that control CGI and discusses methods of CGI manufacturing.

Boiler tubes subjected to cyclic or fluctuating loads over extended periods of time are prone to fatigue failure. Fatigue can occur at relatively low stresses and is implicated in almost 80% of the tube failures in firetube boilers. This chapter covers the most common forms of boiler tube fatigue, including mechanical or vibrational fatigue, corrosion fatigue, thermal fatigue, and creep-fatigue interaction. It discusses the causes, characteristics, and impacts of each type and provides several case studies.

Elevated-temperature failures are the most complex type of failure because all of the modes of failures can occur at elevated temperatures (with the obvious exception of low-temperature brittle fracture). Elevated-temperature problems are real concerns in industrial applications. The principal types of elevated-temperature failure mechanisms discussed in this chapter are creep, stress rupture, overheating failure, elevated-temperature fatigue, thermal fatigue, metallurgical instabilities, and environmentally induced failure. The causes, features, and effects of these failures are discussed. The cooling techniques for preventing elevated-temperature failures are also covered.

This chapter compares and contrasts the high-temperature behaviors of metals and composites. It describes the use of creep curves and stress-rupture testing along with the underlying mechanisms in creep deformation and elevated-temperature fracture. It also discusses creep-life prediction and related design methods and some of the factors involved in high-temperature fatigue, including creep-fatigue interaction and thermomechanical damage.

This chapter explains how the authors assessed the potential risks of creep-fatigue in several aerospace applications using the tools and techniques presented in earlier chapters. It begins by identifying the fatigue regimes encountered in the main engines of the Space Shuttle. It then describes the types of damage observed in engine components and the methods used to mitigate problems. It also discusses the results of analyses that led to changes in design or approach and examines fatigue-related issues in turbine engines used in commercial aircraft.

Fatigue failures occur due to the application of fluctuating stresses that are much lower than the stress required to cause failure during a single application of stress. This chapter describes three basic factors that cause fatigue: a maximum tensile stress of sufficiently high value, a large enough variation or fluctuation in the applied stress, and a sufficiently large number of cycles of the applied stress. The discussion covers high-cycle fatigue, low-cycle fatigue, and fatigue crack propagation. The chapter then discusses the stages where fatigue crack nucleation and growth occurs. It describes the most effective methods of improving fatigue life. The chapter also explains the effect of geometrical stress concentrations on fatigue. In addition, it explores the environmental effects of corrosion fatigue, low-temperature fatigue, high-temperature fatigue, and thermal fatigue. Finally, the chapter discusses a number of design philosophies or methodologies to deal with design against fatigue failures.

This chapter discusses material-related problems associated with coal-fired burners. It explains how high temperatures affect heat-absorbing surfaces in furnace combustion areas and in the convection pass of superheaters and reheaters. It describes how low-NOx combustion technology, intended to reduce NOx emissions, accelerates tube wall wastage. It also covers circumferential cracking in furnace waterwalls, thermal fatigue cracking induced by waterlances and water cannons, superheater-reheater corrosion, and erosion in fluidized-bed boilers.

This article is a detailed account of the mechanisms of fatigue failure of polymers, namely thermal fatigue failure and mechanical fatigue failure. The mechanical fatigue failure is discussed in terms of fatigue crack initiation and fatigue crack propagation.

This chapter describes the phenomenological aspects of fatigue and how to assess its effect on the life of components operating in high-temperature environments. It explains how fatigue is measured and expressed and how it is affected by loading conditions (stress cycles, amplitude, and frequency) and factors such as temperature, material defects, component geometry, and processing history. It provides a detailed overview of the damage mechanisms associated with high-cycle and low-cycle fatigue as well as thermal fatigue, creep-fatigue, and fatigue-crack growth. It also demonstrates the use of tools and techniques that have been developed to quantify fatigue-related damage and its effect on the remaining life of components.