This chapter discusses the critical soldering faults that lead to quality degradation and potential failure of a soldered connection. It then describes the types of nondestructive evaluations used to inspect soldered and brazed joints, including dimensional and visual inspection, ultrasonic testing, radiographic examination, dye penetrant inspection, and leak testing, including overpressure tests. The chapter also provides an overview of destructive physical analysis.

The inspection of castings normally involves checking for shape and dimensions, coupled with aided and unaided visual inspection for external discontinuities and surface quality. This chapter discusses methods for determining surface quality, internal discontinuities, and dimensional inspection. Casting defects including porosity, oxide films, inclusions, hot tears, metal penetration, and surface defects are reviewed. Liquid penetrant inspection, magnetic particle inspection, eddy current inspection, radiographic inspection, ultrasonic inspection, and leak testing for castings are discussed. The chapter provides information on the procedures involved in the inspection of castings that are limited to visual and dimensional inspections, weight testing, and hardness testing. It also discusses the use of computer equipment in foundry inspection operations.

Wrought tubular products are nondestructively inspected chiefly by eddy current techniques (including the magnetic flux leakage technique) and by ultrasonic techniques. The methods discussed in this chapter include eddy current inspection, flux leakage inspection, ultrasonic inspection, magnetic particle inspection, liquid penetrant inspection, and radiographic inspection of resistance welded tubular products, seamless steel tubular products, and nonferrous tubular products. This chapter discusses the fundamental factors that should be considered in selecting a nondestructive inspection method and in selecting from among the commercially available inspection equipment. The factors covered are product characteristics, nature of the flaws, extraneous variables, rate of inspection, end effect, mill versus laboratory inspection, specification requirements, equipment costs, and operating costs.