This chapter discusses the factors that play a role in fatigue failures and how they affect the service life of metals and structures. It describes the stresses associated with high-cycle and low-cycle fatigue and how they differ from the loading profiles typically used to generate fatigue data. It compares the Gerber, Goodman, and Soderberg methods for predicting the effect of mean stress from bending data, describes the statistical nature of fatigue measurements, and explains how plastic strain causes cyclic hardening and softening. It discusses the work of Wohler, Basquin, and others and how it led to the development of a strain-based approach to fatigue and the use of fatigue strength and ductility coefficients. It reviews the three stages of fatigue, beginning with crack initiation followed by crack growth and final fracture. It explains how fracture mechanics can be applied to crack propagation and how stress concentrations affect fatigue life. It also discusses fatigue life improvement methods and design approaches.

Fatigue failures occur due to the application of fluctuating stresses that are much lower than the stress required to cause failure during a single application of stress. This chapter describes three basic factors that cause fatigue: a maximum tensile stress of sufficiently high value, a large enough variation or fluctuation in the applied stress, and a sufficiently large number of cycles of the applied stress. The discussion covers high-cycle fatigue, low-cycle fatigue, and fatigue crack propagation. The chapter then discusses the stages where fatigue crack nucleation and growth occurs. It describes the most effective methods of improving fatigue life. The chapter also explains the effect of geometrical stress concentrations on fatigue. In addition, it explores the environmental effects of corrosion fatigue, low-temperature fatigue, high-temperature fatigue, and thermal fatigue. Finally, the chapter discusses a number of design philosophies or methodologies to deal with design against fatigue failures.

This chapter familiarizes readers with the methods used to quantify the effects of fatigue on component lifetime and failure. It discusses the development and use of S-N (stress amplitude vs. cycles to failure) curves, the emergence of strain-based approaches to fatigue analysis, and important refinements and modifications. It demonstrates the use of approximate equations, including the method of universal slopes and the four-point correlation technique, which provides reasonable estimates of elastic and plastic lines from information obtained in standard tensile tests. It also discusses high-cycle, low-cycle, and ultra-high cycle fatigue and presents several models that are useful for fatigue life predictions.

Mechanical treatments such as grinding and shot peening are often employed in the production of case-carburized parts. Grinding, besides restoring precision, removes carbide films, internal oxidation, and high-temperature transformation products. Shot peening strengthens component surfaces and induces a stress state that increases fatigue resistance. This chapter describes both processes as well as roller burnishing. It explains how these treatments are applied and how they influence the microstructure, properties, and behaviors of case-hardened components. It also addresses process challenges, particularly in regard to grinding.

This chapter provides an overview of factors that must be considered in the design of structural components for satisfactory service performance in terms of mechanical behavior of steel castings. The chapter discusses designing against yielding, excessive deflection, and creep and stress rupture. The chapter describes the three main approaches to evaluating and designing structures relative to fatigue resistance: the S-N curve approach for high cycle fatigue, the strain range approach for low cycle fatigue, and the fracture mechanics approach. Two approaches to design against brittle fracture are described, the ductile to brittle transition concept and the fracture mechanics approach. The chapter also discusses several types of corrosion behavior and emphasizes the need to interact with corrosion specialists in the design process. It illustrates the unique advantages that designers may gain by designing components as castings to achieve low stress concentrations economically.