Although zirconium resists stress-corrosion cracking (SCC) where many alloys fail, it is susceptible in Fe3+- and Cu2+-containing solutions, concentrated HNO3, halogen vapors, mercury, cesium, and CH3OH + halides. This chapter explains how composition, texture, stress levels, and strain rate affect the SCC behavior of zirconium and its alloys. It describes environments known to induce SCC, including aqueous solutions, organic liquids, hot and fused salts, and liquid metals. It also discusses cracking mechanisms and SCC prevention and control techniques.

Hydrogen damage is a form of environmentally assisted failure that results most often from the combined action of hydrogen and residual or applied tensile stress. This chapter classifies the various forms of hydrogen damage, summarizes the various theories that seek to explain hydrogen damage, and reviews hydrogen degradation in specific ferrous and nonferrous alloys. The preeminent theories for hydrogen damage are based on pressure, surface adsorption, decohesion, enhanced plastic flow, hydrogen attack, and hydride formation. The specific alloys covered are iron-base, nickel, aluminum, copper, titanium, zirconium, vanadium, niobium, and tantalum alloys.

The nonferrous alloys described in this chapter include aluminum and aluminum alloys, copper and copper alloys, titanium and titanium alloys, zirconium and zirconium alloys, and tantalum and tantalum alloys. Some of the factors that affect the corrosion performance of welded nonferrous assemblies include galvanic effects, crevices, assembly stresses in products susceptible to stress-corrosion cracking, and hydrogen pickup and subsequent cracking. The emphasis is placed on the compositions, general welding considerations, and corrosion behavior of these alloys.