This chapter reviews some of the differences between powder metallurgy and additive manufacturing and explains how they influence the microstructure and properties of various alloys and the formation of defects in manufactured parts.

Many of the structural characteristics of steel products are a result of changes that occur during solidification, particularly volume contractions and solute redistribution. This chapter discusses the solidification process and how it affects the quality and behaviors of steel. It explains how steel shrinks as it solidifies, causing issues such as pipe and voids, and how differences in the solubility of solid and liquid steel lead to compositional heterogeneities or segregation. It describes the dendritic nature of solidification, peritectic and eutectic reactions, microporosity, macro- and microsegregation, and hot cracking, as well as the effects of solidification and remelting on castings, ingots, and continuous cast products. It explains how to determine where defects originate in continuous casters and how to control alumina, sulfide, and nitride inclusions.

Nickel-base alloys are generally used in harsh environments that demand either corrosion resistance or high-temperature strength. This article first describes the general welding characteristics of nickel-base alloys. It then describes the weldability of solid-solution nickel-base alloys in terms of grain boundary precipitation, grain growth, and hot cracking in the heat-affected zone; fusion zone segregation and porosity; and postweld heat treatments. Next, the article analyzes the welding characteristics of dissimilar and clad materials. This is followed by sections summarizing the various types and general weldability of age-hardened nickel-base alloys. The article then discusses the composition, welding metallurgy, and properties of cast nickel-base superalloys. Finally, it provides information on the welding of dissimilar metals, filler metal selection for welding clad materials and for overlay cladding, service conditions during repair, and welding procedural idiosyncrasies of cobalt-base alloys.