Chapter 9: Life-Assessment Techniques for Combustion Turbines Available to Purchase
-
Published:1989
Page range:
415 - 479
Abstract
Combustion turbines consist of a compressor, a combustor, and a turbine. As commonly configured, the compressor and turbine mount on a single shaft that connects directly to a generator. This chapter reviews the materials of construction, damage mechanisms, and life-assessment techniques for nozzles and buckets. It also presents key information from a detailed review of the literature and the results of a survey on combustion-turbine material problems.
You do not currently have access to this chapter.
Citation
Life-Assessment Techniques for Combustion Turbines, Damage Mechanisms and Life Assessment of High-Temperature Components, By R. Viswanathan, ASM International, 1989, p 415–479, https://doi.org/10.31399/asm.tb.dmlahtc.t60490415
Download citation file:
Related Book Content
Introduction and Overview
Damage Mechanisms and Life Assessment of High-Temperature Components
Life Prediction for Boiler Components
Damage Mechanisms and Life Assessment of High-Temperature Components
Life Assessment of Steam-Turbine Components
Damage Mechanisms and Life Assessment of High-Temperature Components
Petroleum Reactor Pressure-Vessel Materials for Hydrogen Service
Damage Mechanisms and Life Assessment of High-Temperature Components
Nondestructive Evaluation and Life Assessment
Nondestructive Evaluation of Materials
Stress-Corrosion Cracking of an Inconel 600 Safe-End on a Reactor Nozzle
ASM Failure Analysis Case Histories: Power Generating Equipment
Nondestructive Evaluation and Life Assessment
Failure Analysis and Prevention
Leaking Welds in a Ferritic Stainless Steel Wastewater Vaporizer
ASM Failure Analysis Case Histories: Chemical Processing Equipment
Failures of Structures and Components by Metal-Induced Embrittlement
Handbook of Case Histories in Failure Analysis