ASM Failure Analysis Case Histories: Failure Modes and Mechanisms
ASM International
ISBN electronic:
978-1-62708-234-1
Publication date:
2019
Abstract
A crumpled piece of sheet metal had two cracks in a T-junction shape. The relative locations of shear lips in the cracks allowed deduction of which crack happened first, and which direction the cracks propagated.
You do not currently have access to this chapter.
Citation
D. Aliya, Cracking of Sheet Metal, ASM Failure Analysis Case Histories: Failure Modes and Mechanisms, ASM International, 2019, https://doi.org/10.31399/asm.fach.modes.c9001643
Download citation file:
Join ASM International
Being a member of the world’s largest association of materials professionals provides the benefits and resources you need to accomplish your personal and professional goals.
Related Book Content
Cracked Disks of Fan Made of Heat Resistant Steel
ASM Failure Analysis Case Histories: Steelmaking and Thermal Processing Equipment
Dimpling of Aluminium Sheet
ASM Failure Analysis Case Histories: Air and Spacecraft
Grain Disintegration in a Welded Sheet Construction
ASM Failure Analysis Case Histories: Design Flaws
Material Requirements for Service Conditions
Welding, Brazing, and Soldering
Ductile Fracture
Understanding How Components Fail (Third Edition)
Tensile Failure of a Hoist Chain Link
Handbook of Case Histories in Failure Analysis
Failure Analysis of a Helicopter Main Rotor Bolt
Handbook of Case Histories in Failure Analysis
Hydrogen Damage in a Waterwall Boiler Tube Section
Handbook of Case Histories in Failure Analysis
Bulk Workability of Metals
Metalworking: Bulk Forming
Shearing Fracture of a Type 316LR Stainless Steel Screw
ASM Failure Analysis Case Histories: Medical and Biomedical Devices