A steam-pressurized Yankee dryer shell ruptured during normal operation. Cracking had occurred around much of the circumference at the drive end of the shell, which measured 3.7 m (12 ft) in diameter by 3.4 m (11 ft) long with a head bolted to each end. The crack initiated at a 90 deg corner in contact with the edge of the head. The material was a hardened gray cast iron containing 2.8% Ni and 1.2% Mo. Based on the results of visual, nondestructive, metallographic, and chemical analyses, it was concluded that failure occurred after corrosion fatigue cracking had weakened the...
Mark H. Gilkey, Corrosion Fatigue and Subsequent Rupture of a Yankee Dryer Roll on a Modified Paper Machine, Handbook of Case Histories in Failure Analysis, Vol 1, Edited By Khlefa A. Esaklul, ASM International, 1992, p 132–135, https://doi.org/10.31399/asm.fach.v01.c9001050
Download citation file:
Join ASM International
Being a member of the world’s largest association of materials professionals provides the benefits and resources you need to accomplish your personal and professional goals.