Chapter 18: Failure Analysis of Stress-Corrosion Cracking
This chapter describes nondestructive evaluation (NDE) test methods and their relative effectiveness for diagnosing the cause of stress-corrosion cracking (SCC) service failures. It discusses procedures for analyzing various types of damage in carbon and low-alloy steels, high-strength low-alloy steels, hardenable stainless steels, austenitic stainless steels, copper-base alloys, titanium and titanium alloys, aluminum and aluminum alloys, and nickel and nickel alloys. It identifies material-environment combinations where SCC is known to occur, provides guidelines on how to characterize cracking and fracture damage, and explains what to look for during macroscopic and microscopic examinations as well as chemical and metallographic analyses. It...
M.A. Torres, S.W. Stafford, S.L. Smith, Failure Analysis of Stress-Corrosion Cracking, Stress-Corrosion Cracking: Materials Performance and Evaluation, 2nd ed., Edited By Russell H. Jones, ASM International, 2017, p 419–442, https://doi.org/10.31399/asm.tb.sccmpe2.t55090419
Download citation file:
Understanding the Basics Collection
8-Volume Digital Library Exclusive!
The Understanding the Basics Collection provides comprehensive coverage of critical topics in metallurgy. These introductory guides present critical information on key topics related to materials processing, performance, and evaluation..