A 10%Cr martensitic steel for rotor applications, COST FB2, was used in 620°C steam turbines for about four years in China. In order to increase the unit efficiency to 50% of the coal-fired power plant, an advanced 630°C steam turbine developed by DongFang Turbine Co., Ltd will be put into operation in 2021. A three-ton middle-scale prototype turbine rotor forging (3387FC1) was developed and evaluated through the collaborative work of DongFang Turbine and the Japan Steel Works (JSW) using JMATR, a high-performance heat-resistant steel developed by JSW. Test results for the prototype rotor, including homogeneity of chemical composition, ultrasonic tests, mechanical properties, and long-term creep behaviors, and microstructure, are presented and discussed.

The trial production of FENIX-700 turbine rotors for advanced-ultra super critical (A-USC) power generation was conducted, and their microstructure, tensile, impact, and creep properties were evaluated. Two 10-ton class trial forgings were successfully produced through double melting of VIM and ESR and free forging with a 14,000 ton hydraulic press. For examining the effect of the forging condition on the microstructure of the rotors, we adopted lower finish temperatures and an increased forging ratio on the last forging for the second trial. The grains of the second trial forging were refined by changing the forging condition. In particular, the grain size of the center of the rotor was remarkably decreased from the grain size number 0.5 to 2.8. Grain refinement improved the permeability of the ultrasonic wave in the ultrasonic inspection test, resulting in decreasing the minimum detectable flaw size (MDFS). The ductility and toughness were also improved by grain refinement. Although the grain size was decreased, the time to rupture in the creep test at 700 °C was comparable to the previous results of FENIX-700, and the estimated 105 h rupture stress at 700 °C was sufficiently higher than 100 MPa. However, it was clarified that the particles of gamma-prime in the center of the rotor had been coarsened due to the mass effect. The slight decrease of 0.2% proof stress and shortening of creep rupture time at 700 °C were attributed to the coarse gamma-prime particles. The results of the present trial expressly demonstrated that it is possible to manufacture 10-ton class A-USC turbine rotors of FENIX-700 with excellent mechanical properties and good permeability of the ultrasonic wave.

The effect of grain size after solution treatment on the mechanical properties of FENIX-700, including its cooling rate, was investigated. In addition, the dependance of precipitation observed at grain boundaries on the heat treatment conditions was also discussed on the basis of the results of microstructure observations. It was confirmed that the tensile ductility, the creep rupture ductility, and the absorbed energy decreased as the grain size increased. The creep rupture strength, in contrast, increased remarkably as the grain size increased. The tensile strength increased as the cooling rate increased. Experimental results showed that satisfactory mechanical properties would be obtained for a grain size of ASTM G.S.No. 1.0-3.0.

A modified version of Alloy 706, designated FENIX-700, was developed using the CALPHAD method to improve high-temperature stability above 700°C. The new alloy features reduced Nb and increased Al content, relying on γ' (Ni 3 Al) strengthening while eliminating γ'' (Ni 3 Nb), δ, and η phases. This modification improved both creep temperature capability (from 650°C to 700°C) and segregation properties. Successful manufacturing trials included a 760 mm² forging shaft using triple melt processing and a 1050 mm ESR ingot, demonstrating industrial viability. The study also explores compatible Ni-base welding materials for joining FENIX-700 to 12% Cr ferritic steel in 700°C class steam turbine applications.