Oxide scale formation in the inner bore of steam tubing has been identified as a key metric for determining operational parameters and life expectancy of modern boiler systems. Grade 91 tubing is commonly used for the construction of key components within boiler systems designed for power generation operating in the temperature range of 500 to 650 °C. Standard laboratory test procedures involve grinding the surface of test coupons to homogenise their surface structure and improve experimental consistency, however, data presented here shows a discrepancy between laboratory and industrial practices that has long term implications on scale growth kinetics and morphological development. Microstructural analysis of both virgin and ex-service tubing reveals the presence of a pre-existing oxide structure that is incorporated into the inwardly growing scale and is implicated in the formation of multiple laminar void networks. These void networks influence thermal diffusivity across the scale and may function as regions of spallation initiation and propagation.

The drive for increased efficiency and carbon reduction in next-generation boilers is pushing conventional materials to their limits in terms of strength and oxidation resistance. While traditional isothermal testing of simple coupons provides some insight into material performance, it fails to accurately represent the heat transfer conditions present in operational boilers. This paper introduces a novel test method designed to evaluate the degradation of candidate materials under more realistic heat flux conditions. The method, applied to tubular specimens using both laboratory air and steam as cooling media, demonstrates a significant impact of thermal gradients on material performance. Initial comparisons between tubular heat flux specimens and flat isothermal specimens of 15Mo3 revealed increased oxidation kinetics and altered oxide morphology under heat flux conditions. The paper details the design of this heat flux test, presents results from initial work on 15Mo3 under air and steam conditions, and includes findings from further studies on oxides formed on 2-1/4Cr material under both heat flux and isothermal conditions. This research represents a crucial step toward more accurate prediction of material behavior in next-generation boiler designs.

This paper outlines a comprehensive UK-based research project (2007-2010) focused on developing fireside corrosion models for heat exchangers in ultra-supercritical plants. The study evaluates both conventional materials like T22 and advanced materials such as Super 304H, examining their behavior under various test environments with metal skin temperatures ranging from 425°C to 680°C. The research aims to generate high-quality data on corrosion behavior for materials used in both furnace and convection sections, ultimately producing reliable corrosion prediction models for boiler tube materials operating under demanding conditions. The project addresses some limitations of existing models for these new service conditions and provides a brief review of the fuels and test environments used in the program. Although modeling is still limited, preliminary results have been presented, focusing on predicting fireside corrosion rates for furnace walls, superheaters, and reheaters under various service environments. These environments include those created by oxyfuel operation, coal-biomass co-firing, and more traditional coal firing.