For the safe operation of high temperature equipment, it is necessary to ensure creep rupture ductility of the components from the viewpoint of notch weakening. In this study, the effect of heat treatment conditions on creep rupture ductility was evaluated and its underlying metallurgical mechanism was investigated with using a forged Ni-based superalloy Udimet520. In order to improve the creep rupture ductility without lowering the creep rupture strength, it is important to increase both intragranular strength and intergranular strength in a balanced manner. For this purpose, it was clarified that 1) secondary γ' phase within grains should be kept fine and dense, 2) grain boundaries should be sufficiently covered by M 23 C 6 carbide by increasing its phase fraction, and 3) tertiary γ' phase within grains should be redissolved before the start of creep. To obtain such a precipitate state, it is essential to appropriately select the cooling rate after solution treatment, stabilizing treatment and aging treatment conditions.

Advanced 700°C-class steam turbines demand austenitic alloys for superior creep strength and oxidation resistance beyond 650°C, exceeding the capabilities of conventional ferritic 12Cr steels. However, austenitic alloys come with a higher coefficient of thermal expansion (CTE) compared to 12Cr steels. To ensure reliability, operability, and performance, these advanced turbine alloys require low CTE properties. Additionally, for welded components, minimizing CTE mismatch between the new material and the welded 12Cr steel is crucial to manage residual stress. This research investigates the impact of alloying elements on CTE, high-temperature strength, phase stability, and manufacturability. As a result, a new material, “LTES700R,” was developed specifically for steam turbine rotors. LTES700R boasts a lower CTE than both 2.25Cr steel and conventional superalloys. Additionally, its room-temperature proof strength approaches that of advanced 12Cr steel rotor materials, while its creep rupture strength around 700°C significantly surpasses that of 12Cr steel due to the strengthening effect of gamma-prime phase precipitates. To assess the manufacturability and properties of LTES700R, a medium-sized forging was produced as a trial run for a turbine rotor. The vacuum arc remelting process was employed to minimize segregation risk, and a forging procedure was meticulously designed using finite element method simulations. This trial production resulted in a successfully manufactured rotor with satisfactory quality confirmed through destructive evaluation.

Advanced 700C class steam turbines require austenitic alloys instead of conventional ferritic heat-resistant steels which have poor creep strength and oxidation resistance above 650C. Austenitic alloys, however, possess a higher thermal expansion coefficient than ferritic 12Cr steels. Therefore, Ni-based superalloys were tailored to reduce their coefficients to the level of 12Cr steels. Regression analysis of commercial superalloys proves that Ti, Mo and Al decrease the coefficient quantitatively in this order, while Cr, used to secure oxidation resistance, increases it so significantly that Cr should be limited to 12wt%. The newly designed Ni-18Mo-12Cr-l.lTi-0.9Al alloy is strengthened by gamma-prime [Ni 3 (Al,Ti)] and also Laves [Ni 2 (Mo,Cr)] phase precipitates. It bears an RT/700C mean thermal expansion coefficient equivalent to that of 12Cr steels and far lower than that of low-alloyed heat resistant steels. Its creep rupture life at 700C and steam oxidation resistance are equivalent to those of a current turbine alloy, Refractaloy 26, and its tensile strength at RT to 700C surpasses that of Refractaloy 26. The new alloy was trial produced using the VIM-ESR melting process and one ton ingots were successfully forged into round bars for bolts without any defects. The bolts were tested in an actual steam turbine for one year. Dye penetrant tests detected no damage. The developed alloy will be suitable for 700C class USC power plants.