Structural changes in P92-type steel after creep at temperature of 600°C under a stress of 140 MPa were investigated. The steel was solution treated at 1050°C and tempered at 780°C. The structure in the grip portion of the creep specimen changed scarcely after creep exposure for 6876 h. In contrast, the structural changes in the gage and neck sections were characterized by transformation of the tempered martensite lath structure into relatively coarse subgrain structure. The formation of a well-defined subgrain structure in the gage and neck sections was accompanied by the coarsening of M 23 C 6 carbides and precipitations of Laves phase during creep. Mechanisms of grain boundary pinning by precipitates are discussed.

Microstructure in the gage sections of ruptured GX12CrMoWVNbN10-1-1 cast steel specimens was examined after creep tests under applied stresses ranging from 120 to 160 MPa at T=893 K. The microstructure after tempering consisted of laths with an average thickness of 332 nm. The tempered martensite lath structure was characterized by M 23 C 6 -type carbide particles with an average size of about 105 nm, and MX carbonitrides with an average size of about 45 nm. Precipitation of Laves phase occurred during creep test. The structural changes in the gauge section of the samples were characterized by the evolution of relatively large subgrains with remarkably lowered density of interior dislocations within former martensite laths. MX carbonitrides and M 23 C 6 -type carbide particles increase in size slightly under long-term creep. Microstructural degradation mechanisms during creep in GX12CrMoWVNbN10-1-1 cast steel are discussed.

The effect of multiple hot rolling in the temperature interval of 700-1000°C (1290-1830°F) on microstructures and tensile behavior of an S304H-type austenitic stainless steel was studied. The structural changes during hot working are characterized by the elongation of original grains towards the rolling axis and the development of new fine grains. The fraction of fine grains and the average grain size increase with increasing the rolling temperature. The multiple hot rolling results in significant strengthening. The offset yield strength approaches 1080 MPa in the sample processed at 700°C (1290°F), while that of 390 MPa is obtained after rolling at 1000°C (1830°F). On the other hand, the tensile strength at elevated temperatures of 600-700°C (1110-1290°F) decreases with a decrease in the rolling temperature. The relationship between the deformation structures and the tensile behavior is considered in some detail.