This study investigates the influence of build orientation on the high-temperature mechanical properties of IN738LC manufactured via metal laser powder bed fusion (PBF-LB/M). Since the PBF-LB/M layer-wise manufacturing process significantly affects grain morphology and orientation—ranging from equiaxed to textured grains—mechanical properties typically exhibit anisotropic behavior. Samples were manufactured in three build orientations (0°, 45°, and 90°) and subjected to hot tensile and creep testing at 850°C following DIN EN ISO 6892-2 and DIN EN ISO 204 standards. While tensile properties of the 45° orientation predictably fell between those of 0° and 90° orientations, creep behavior over 100-10,000 hours revealed unexpected results: the 45° orientation demonstrated significantly shorter rupture times and faster creep rates compared to other orientations. Microstructural analysis revealed distinct creep deformation mechanisms active within different build orientations, with the accelerated creep rate in 45° specimens attributed to multiple phenomena, particularly η-phase formation and twinning. These findings provide crucial insights into the orientation-dependent creep behavior of PBF-LB/M-manufactured IN738LC components.

Cast nickel-based superalloys used as structural materials for gas turbine parts need to withstand high temperatures and dynamic mechanical loads. When in contact with ambient air, the formation of protective oxide scales causes a depletion of γ’-precipitates in the surface-near region and leaves a weakened microstructure. This environmentally based degradation of the material might be accelerated under cyclic thermal exposure. In this paper, the cyclic oxidation behavior of two cast nickel-based superalloys and one single crystalline variant are investigated: C1023, CM-247 LC and M-247 SX. Exposure tests were carried out under both isothermal and cyclic conditions in air at 850 °C, 950 °C and 1050 °C for times up to 120 h to investigate the impact of thermal cycling. The differences in oxidation mechanisms are analyzed phenomenologically via light and electron microscopy and brought in correlation with the oxidation kinetics, determined based on net mass change and depletion zone growth. An assessment of the impact of precipitation loss on local mechanical strength is attempted via nano-indentation method. The found relations can be transferred onto an acceleration of crack growth under creep-fatigue and thermo-mechanical fatigue conditions.

Detailed knowledge of the creep and creep crack behavior is essential for a safe operation of thick-walled components in thermal power plants. High mechanical loads and temperatures of more than 700 °C often require the application of nickel-based alloys, e.g. alloy C-263. Unfortunately, manufacturing and non-destructive evaluation (NDE) of thick-walled components (> 50 mm) made of nickel-based alloys are quite challenging. Tolerable critical flaw sizes, experimentally validated for long service durations, play an important role in the quality assurance of such components. It is commonly accepted that manufacturing parameters, e.g. heat treatment procedures, have a significant influence on creep ductility and time-dependent crack behavior. By means of adjusting the process parameters, the ductility and the creep life of notched specimen can be significantly improved in the case of alloy C-263. Essential root cause is the decoration of grain boundaries with carbides which drastically influences creep crack initiation and growth. This results in significant differences for allowable critical flaw sizes and thus, the potential use of the candidate material. On a first generation of alloy C-263 “G1”, a dense population of carbides on the grain boundaries was found, which resulted in an inadmissible creep crack behavior. The resulting critical flaw sizes were only a few tenths of a millimeter. On a second generation “G2”, the grain boundary occupation was positively influenced, so that a satisfactory creep crack behavior could be found. The critical flaw sizes are in the order of one millimeter or more. A critical or impermissible material behavior under creep conditions can be demonstrated by testing smooth and notched round specimens. For example, the first generation “G1” notched round specimens fails earlier than the smooth round specimens, indicating notch sensitivity. On the second generation “G2”, however, a notch insensitivity was found. The critical defect sizes can be determined by a method that takes into account a simultaneous examination of the crack tip situation and the ligament situation.

Especially for industrial applications like pumps, mining or off shore industries, where high demands on the abrasive properties of the materials are required, thermal sprayed Fe-based coatings become increasingly important. Novel FeCrMnBC alloys, which have economic and ecological advantages compared to Ni-based or Co-based coatings, are in the focus of this work. In order to produce adequate coatings with a three-cathode plasma torch, different powder fractions (-45+20 μm, -25+10 μm) and varying chemical composition of FeCrMnBC coatings have been investigated and compared with respect to corrosion, abrasion, and erosion properties. In case of wear reduction, selected coatings were additionally subsequent plasma nitrided to study the effect of this treatment on coating morphology and microstructure. The corrosion and tribological behavior were investigated by means of current/density potential curve measurements and ball-on-disc experiments in view of wear morphologies. Erosion-corrosion behavior has been investigated in a pump test rig with 10 wt.-% solid content of corundum in artificial sea water. In general, samples with small powder fractions exhibit accelerated corrosion and decreased erosion behavior, based on their microstructural characteristics. Plasma nitrided coatings show a decrease in corrosion and erosion resistance, which is presumably due to partial formation of chromium carbide in the coatings. Based on the results, the advantages and disadvantages of FeCrMnBC coatings for the application as wear and corrosion protection of complex pump parts are discussed with respect to varied parameters.

In order to enable a compact design for boiler superheaters in modern thermal power plants, cold-worked tube bending is an economical option. For service metal temperatures of 700 °C and above, nickel-based alloys are typically employed. To ensure a safe operation of such cold-worked alloys, their long-term mechanical behavior has to be investigated. In general, superheater tube materials in a cold-worked state are prone to a degradation of their long-term creep behavior. To predict this degradation, sensitive experiments have to be conducted. In this publication, the effects of cold working on the long-term creep behavior of three currently used nickel-based alloys are examined. Creep and creep rupture experiments have been conducted at typical service temperature levels on nickel-based alloys, which have been cold worked to various degrees. As a result, Alloy 263 exhibits no significant influence of cold working on the creep rupture strength. For Alloy 617, an increase of creep strength due to cold working was measured. In contrast, Alloy 740 showed a severe degradation of the creep strength due to cold working. The mechanism causing the sensitivity to cold working is not yet fully understood. Various formations of carbide precipitates at the grain boundaries are believed to have a major influence. Nevertheless, the experimentally observed sensitivity should always be considered in material selection for boiler tube design.

A material test loop has been installed at GKM Mannheim, which enables thick-walled components of future highly-efficient power plants to be exposed to steam temperatures of up to 725 °C. The project goal was to demonstrate the feasibility of a 700 °C power plant.

For safe operation of thick-walled components for Advanced Ultra Super Critical (A-USC) power plants, detailed knowledge of the creep crack initiation and growth behavior is essential. The high loading and high temperature conditions in an A-USC power plant require, in many cases, the employment of nickel base super alloys. Unfortunately, both manufacturing and nondestructive evaluation (NDE) of thick-walled components (> 50 mm) made of nickel base super alloys are quite challenging. In this paper, one candidate material for such applications, Alloy C-263, was tested for creep and creep crack behavior at 700 °C. Objective of the study was to determine a critical flaw size. In order to establish this size, the duration to achieve the 1%-strain limit at a given load is compared with the time to grow the initial flaw for Δa = 0.5 mm when the component was loaded with the same given load. It will be shown that manufacturing parameters, e. g. heat treatment procedures, have a significant influence on the creep crack initiation and growth behavior and thus on component life. Decoration of grain boundaries with precipitates, for instance caused by the manufacturing process, can reduce the creep crack resistance and thus increase the risk for premature component failure.

To improve efficiency and flexibility and reduce CO 2 emissions, advanced ultra super critical (AUSC) power plants are under development, worldwide. Material development and its selection are critical to the success of these efforts. In several research and development programs / projects the selection of materials is based on stress rupture, oxidation and corrosion tests. Without doubt, these criteria are important. To improve the operational flexibility of modern power plants the fatigue properties are of increased importance. Furthermore, for a safe operation and integrity issues the knowledge about the crack behavior is essential. Crack initiation and crack growth may be caused by natural flaws or cracks induced by component operation. In order to develop new materials, properties like tensile strength and creep strength are an important part of qualification and subsequent approval by notified bodies. Consequently short term properties as well as time-temperature dependent properties are generated and taken into considerations. In the case of high strength γ'-strengthening nickel-base alloys investigating the creep crack behavior is also strongly recommended. This article shows results of currently investigated nickel-based alloys for newly developed headers, pipes and other high temperature boiler applications and their critical creep crack propagation behavior.