This study investigates how temperature affects the plasticity and thermal creep behavior of 347H stainless steel under uniaxial tension. The research combined experimental testing with advanced computational modeling. Two types of experiments were conducted: uniaxial tensile tests at temperatures from 100°C to 750°C using strain rates of ~10⁻⁴ s⁻¹, and creep tests at temperatures between 600°C and 750°C under various stress levels. These experimental results were used to develop and validate a new integrated mechanistic model that can predict material behavior under any loading condition while accounting for both stress and temperature effects. The model was implemented using a polycrystalline microstructure simulation framework based on elasto-viscoplastic Fast Fourier Transform (EVPFFT). It incorporates three key deformation mechanisms: thermally activated dislocation glide, dislocation climb, and vacancy diffusional creep. The model accounts for internal stress distribution within single crystals and considers how precipitates and solute atoms (both interstitial and substitutional) affect dislocation movement. After validation against experimental data, the model was used to generate Ashby-Weertman deformation mechanism maps for 347H steel, providing new insights into how microstructure influences the activation of different creep mechanisms.

Modern polycrystalline Ni-base superalloys for advanced gas turbine engines have been a key component that has contributed to technological advances in propulsion and power generation. As advanced turbine engine designs are beginning to necessitate the use of materials with temperature and strength capabilities beyond those exhibited by existing materials, new alloying concepts are required to replace conventional Ni-base superalloys with conventional γ-γ’ microstructures. The phase stability of various high Nb content Ni-base superalloys exhibiting γ-γ’-δ -η microstructures have been the subject of a number of recent investigations due to their promising physical and mechanical properties at elevated temperatures. Although high overall alloying levels of Nb, Ta and Ti are desirable for promoting high temperature strength in γ-γ’ Ni-base superalloys, excessive levels of these elements induce the formation of δ and η phases. The morphology, formation, and composition of precipitate phases in a number of experimental alloys spanning a broad range of compositions were explored to devise compositional relationships that can be used to predict the microstructural phase stability and facilitate the design of Ni-base superalloys.