Monoblock low-pressure (LP) turbine rotor shaft forgings for nuclear power plants have been produced from up to 600 ton ingots. However, ingots greater than 600 tons are necessary to increase the generator capacity. Segregation, non-metallic inclusions, and micro porosities inevitably increase with the increase in ingot size. Manufacturing such massive ingots with high soundness is quite difficult. Thus, the development of 650 ton ingot production was carried out in 2010. The 650 ton ingot was dissected and investigated to verify its internal quality. The internal quality of the 650 ton ingot was found to be equal to that of 600 ton ingots. Subsequently, in 2011, we produced a 670 ton ingot, the world’s largest, to produce a trial LP rotor shaft forging with a diameter of 3,200 mm. Results show that the internal quality, mechanical properties, and heat stability are the same as LP rotor shaft forgings made from 600 ton ingots.

A modified version of Alloy 706, designated FENIX-700, was developed using the CALPHAD method to improve high-temperature stability above 700°C. The new alloy features reduced Nb and increased Al content, relying on γ' (Ni 3 Al) strengthening while eliminating γ'' (Ni 3 Nb), δ, and η phases. This modification improved both creep temperature capability (from 650°C to 700°C) and segregation properties. Successful manufacturing trials included a 760 mm² forging shaft using triple melt processing and a 1050 mm ESR ingot, demonstrating industrial viability. The study also explores compatible Ni-base welding materials for joining FENIX-700 to 12% Cr ferritic steel in 700°C class steam turbine applications.