The effect of grain size after solution treatment on the mechanical properties of FENIX-700, including its cooling rate, was investigated. In addition, the dependance of precipitation observed at grain boundaries on the heat treatment conditions was also discussed on the basis of the results of microstructure observations. It was confirmed that the tensile ductility, the creep rupture ductility, and the absorbed energy decreased as the grain size increased. The creep rupture strength, in contrast, increased remarkably as the grain size increased. The tensile strength increased as the cooling rate increased. Experimental results showed that satisfactory mechanical properties would be obtained for a grain size of ASTM G.S.No. 1.0-3.0.

A new Ni-base superalloy has been developed for Advanced Ultra Super Critical (A-USC) power plants operating above 750°C, targeting reduced CO 2 emissions through improved efficiency. While existing research focuses on 700°C-class materials, this study presents a novel alloy design for higher-temperature applications. Using the CALPHAD method, a prototype alloy (Ni-23Co-18Cr-8W-4Al-0.1C) was developed by eliminating Ti, Nb, and Ta to improve hot-workability while maintaining strength. The resulting alloy demonstrates twice the creep strength of Nimonic 263, with an estimated 10 5 h steam turbine creep resistance temperature of 780°C, marking a significant advancement in A-USC material capabilities.

A modified version of Alloy 706, designated FENIX-700, was developed using the CALPHAD method to improve high-temperature stability above 700°C. The new alloy features reduced Nb and increased Al content, relying on γ' (Ni 3 Al) strengthening while eliminating γ'' (Ni 3 Nb), δ, and η phases. This modification improved both creep temperature capability (from 650°C to 700°C) and segregation properties. Successful manufacturing trials included a 760 mm² forging shaft using triple melt processing and a 1050 mm ESR ingot, demonstrating industrial viability. The study also explores compatible Ni-base welding materials for joining FENIX-700 to 12% Cr ferritic steel in 700°C class steam turbine applications.