Cu needs a higher level of ultrasound combined with bonding force to be bonded to the Al pad properly, not just because Cu is harder than Au, but it is also harder to initiate intermetallic compounds (IMC) formation during bonding. This increases the chances of damaging the metal/low k stack under the bondpad. This paper presents a fundamental study of IMC as well as one example of a failure mode of Cu/Al bonded devices, all based on detailed analysis using scanning electron microscopy, scanning transmission electron microscopy, energy dispersive spectrometers, and transmission electron microscopy. It presents a case study showing a corrosion mechanism of Cu/Al ballbond after 168hr UHAST stress. It is observed that all Cu9Al4 was consumed, while very little copper aluminide remained after 168 hours of UHAST stressing.

This paper presents decapsulation solutions for devices bonded with Cu wire. By removing mold compound to a thin layer using a laser ablation tool, Cu wire bonded packages are decapsulated using wet chemical etching by controlling the etch time and temperature. Further, the paper investigates the possibilities of decapsulating Cu wire bonded devices using full wet chemical etches without the facilitation of laser ablation removing much of mold compound. Additional discussion on reliability concerns when evaluating Cu wirebond devices is addressed here. The lack of understanding of the reliability of Cu wire bonded packages creates a challenge to the FA engineer as they must develop techniques to help understanding the reliability issue associated with Cu wire bonding devices. More research and analysis are ongoing to develop appropriate analysis methods and techniques to support the Cu wire bonding device technology in the lab.