In order to explore wear properties of Ni-based coating on the copper substrate, the coatings with different composition were designed. Ni-based coating, Ni-based/Al 2 O 3 and Ni-based/Al 2 O 3 /WC coatings were sprayed by HVAF on the copper substrates. Wear properties of different composite coating were measured at different loads at room temperature. The experimental results indicate that all the coatings have high wear resistance. Adding Al 2 O 3 in sprayed powders has little effect on the microstructures and wear properties of coating. The wear resistant is improved by the addition WC-12Co obviously. The best wear resistant is obtained when optimum WC-12Co content is added.

Plasma sprayed chromium oxides coatings have been widely applied in anilox rolls and pump seal for many years. This paper is researching the effect of nanostructured Cr 2 O 3 5SiO 2 3TiO 2 composite powder preparation when adding nano-size SiO 2 and TiO 2 powder in Cr 2 O 3 powder, to prepare for through spray drying, high temperature sintering and flame density. The microstructure of powder and plasma sprayed coating are analyzed by SEM and XRD, compared with pure Cr 2 O 3 powder and METCO 136F powder. The Microhardness of the coatings are measured by 402MVA TM Vickers hardness tester. Fracture test is used to analysis the ductility of coatings, and the fracture appearance is analyzed by SEM. The result indicates that the mechanical behaviors of nanostructured Cr 2 O 3 5SiO 2 3TiO 2 coating has better performance in the nature of hardness and ductility.

HVO/AF (High-Velocity-Oxygen/Air-Fuel) WC-17Co and WC-10Co4Cr coatings exhibit great potential in the replacement of electrolytic hard chrome (EHC) coating, and comprehensive properties of such coatings should be not worse than those of electrolytic hard chrome coating. The impingement-resistance of HVAF coatings sprayed on 300M ultra-high strength steel was studied in this paper. As an important property index, the fracture toughness of HVAF WC coatings was measured using micro-indentation method at the load of 9.8, 19.6, 24.5, 29.4 and 49.0N respectively. The cracks resulted from stress concentration in the micro-indentation were analyzed. The impingement-resistance for two HVAF WC coatings and EHC was evaluated according to the ASTM D3170 standard, and steel ball dropping experimentation was performed at the height of 0.61, 1.52, 1.83, 2.36 and 2.59m respectively. The cracks caused by both impingements were analyzed using SEM and optical microscopy in comparison with cracks in micro-indentation test.

The influence of the high velocity air fuel (HVAF) sprayed coating on the fatigue behavior of the low alloy steel was studied at different stress levels. It was observed that only one single main crack initiator existed in the substrate after fatigue at low stress levels, but there were multi-cracks on the substrate surface at high stress level. Detailed investigations showed that the cracks in the HVAF coatings sinuously extended to the interface and deflected thereat along the interface. Consequently, free-standing coating was formed due to its limited bond strength to the substrate and the lower elastic modulus than that of the substrate. The gap between the free-standing coating and the substrate surface was found to be correlated with the stress level. The high stress can greatly degrade the adhesion to the substrate causing the delamination of the coating. The cracks in the HVAF coating had no significant effect on the fatigue life of the substrate.

With the incoming of HVOF, the coating properties and application extent of WC-Co type have been greatly improved, in the recent years, we found that the characteristics of WC-Co powder has some influence on its coating properties prepared by HVOF. In this paper, study has been prepared on powders made from aboard and Beijing General Research Institute of Mining & Metallurgy properties such as fluidity, aspect, profile of coating SEM and carbon content, also phase structure and properties analysis of HVOF coating has been made. Finally, influence of powder preparing technology and HVOF technology parameters of different powders for coating properties have been described.