A research program has been initiated to develop the first predictive methodology for corrosion fatigue life in steam turbine blades, addressing a critical gap in current understanding despite extensive research into corrosion pitting and fatigue failure. The study focuses initially on dual-certified 403/410 12% Cr stainless steel, utilizing a newly developed test facility capable of conducting high-cycle fatigue tests in simulated steam environments at 90°C with controlled corrosive conditions. This testing platform enables the investigation of various steady and cyclic stress conditions, establishing a foundation for future testing of other blade steels and the development of comprehensive blade life estimation techniques.