Erosion-corrosion is a severe problem observed in the coal fired thermal power plant boilers which lead to premature failure of boiler tubes. Thermal spray coatings have been applied successfully to check the erosion-corrosion of boiler tubes. In the present research work NiCrTiCRe coating powders were successfully deposited on T22 boiler steel by two different coating processes i.e. high velocity oxy-fuel (HVOF) and cold spray process. The performance of the coatings in actual power plant boiler were investigated and compared. The uncoated and coated T22 boiler steels were subjected the superheater zone of the coal fired boiler for a total of 15 consequent cycles. The thickness loss data and weight change analysis were used to establish kinetics of the erosion-corrosion. X-ray diffraction, surface field emission scanning electron microscope/energy dispersive spectroscopy (FE-SEM/EDS) techniques were used in the present work for the analysis. The results of thickness loss data indicated that the cold sprayed coating performed better in thermal power plant boiler environment.

Detonation-gun spray technology is a novel coating deposition process which is capable of achieving very high gas and particle velocities approaching 4-5 times the speed of sound. This process provides the possibility of producing high hardness coatings with significant adherence strength. In the present study, this technique has been used to deposit WC-Co coatings on T22 boiler steel. Investigations on the oxidation performance of detonation-sprayed WC-Co coatings in air and in molten salt Na 2 SO 4 -82Fe 2 (SO 4 ) 3 at 700°C under cyclic conditions have been carried out. The thermogravimetric technique was used to establish the kinetics of corrosion. The uncoated boiler steel suffered a catastrophic corrosion in the form of intense spalling of its oxide scale during air, as well as, molten salt induced oxidation. The WC-Co coated specimens showed lesser overall weight gains in comparison to their uncoated counterparts in both the environments. The oxidation kinetics for the coated specimens followed nearly the parabolic rate law. The overall weight gain has been found to be higher in the case of air oxidation as compared to that in salt environment for all the cases. Scanning electron microscopy/energy-dispersive spectroscopy (SEM/EDS) techniques were used to analyse the corrosion products, which indicated the formation of W and O as main elements in the oxide scales of the coated steel in both the environments.

In this investigation, Ni-20Cr alloy powder was deposited on SA 516 boiler steel by cold spraying. The oxidation kinetics of both coated and uncoated samples, evaluated in molten salt, followed a parabolic rate. The rate constant of the Ni-20Cr coated steel was much lower than that of the bare boiler steel. X-ray diffraction, SEM-EDX, and X-ray mapping were used to analyze the oxidation products of the coated and uncoated boiler steel. The uncoated steel exhibited intense spalling and peeling of its oxide scale, which may be due to the formation of Fe 2 O 3 oxides. The Ni-20Cr coating reduced the weight gain of the steel by more than 87% possibly due to the formation of nickel and chromium oxides.

The aim of this study is to investigate the role of zirconium (Zr) in HVOF coatings in order to formulate a high-temperature oxidation-resistant composition. Ni-20Cr coatings with and without 1% Zr additions were deposited on 347H boiler steel by HVOF spraying and their oxidation behavior was assessed at a temperature of 900 °C under cyclic conditions. Test specimens were also subjected to actual boiler environments to ascertain their erosion-corrosion behavior. Weight change measurements were used to determine high-temperature oxidation kinetics as well as erosion-corrosion resistance. The specimens were examined after each thermal cycle to observe physical changes and spallation in their oxide scales. It was found that the addition of Zr in the Ni-20Cr coating reduced the oxidation rate but had little effect on erosion-corrosion resistance.

In this study, HVOF thermal spray technique was used to deposit Ni-20Cr coating on a commonly used boiler steel ASTM-SA213-T22.The specimens with and without coating were subjected to cyclic oxidation testing at an elevated temperature of 900°C to ascertain usefulness of the coating for 50 cycles. Each cycle consisted of 1 hour heating in a silicon carbide tube furnace followed by 20 min cooling in air. Mass change technique was used to approximate the kinetics of oxidation. The uncoated sample suffered intensive spallation along with a significant overall mass gain. The oxidation rate was found to reduce appreciably after the deposition of the coating by 91%. The exposed specimens were characterized by X-ray diffraction [XRD] and scanning electron microscopy/energy dispersive spectroscopy [SEM/EDS]. It was observed that HVOF-sprayed Ni-20Cr coating was suitable to provide oxidation resistance to the given steel in the air environment.

A study was carried out to determine the role of HVOF-spray Ni-20Cr coatings to enhance high temperature oxidation resistance of T22 and 347H boiler steels. Ni-20Cr coatings were deposited on the boiler steels. Subsequently high temperature oxidation behavior of these coatings was investigated by laboratory tests at an elevated temperature of 9000C under cyclic conditions. These coatings were also subjected to a boiler environment at an elevated temperature of 700ºC under cyclic conditions to ascertain their erosion-corrosion behaviour. Thermogravimetric data was taken after each cycle to formulate the oxidation, as well as, erosion-corrosion kinetics. The specimens were also physically examined after each cycle to notice any macrographic physical changes, spallation tendency of their oxide scales etc. The exposed specimens were examined using scanning electron microscopy and Energy Dispersive Spectroscopy (SEM/EDS) analysis. It was observed that oxidation rate was subsequently low in the coated substrates as compare to uncoated steels. It was observed that Ni-20Cr coating on 347H boiler substrate showed the maximum oxidation resistance. Moreover, both the steels showed better resistance to erosion-corrosion in actual boiler conditions after the application of Ni-20Cr coating.

In the present work, commercially available NiCr and NiCr-TiC powder blends were deposited on boiler steel substrates by HVOF spraying. To evaluate coating performance, bare and coated steel samples were placed in the superheater zone of a coal fired boiler for 15 cycles. Weight change and thickness loss were measured and the results were used to establish erosion-corrosion kinetics. XRD and SEM/EDS techniques were used to analyze the microstructure and phase composition of as-sprayed and eroded-corroded specimens. The improvement in erosion-corrosion resistance provided by the coating may be attributed to the formation of nickel and chromium oxides and spinels.

The significant erosion of the boiler tube at high temperature becomes an important problem for the safe operation of circulating fluidized bed boiler. This paper investigated the erosion behavior of the HVOF sprayed Cr 3 C 2 -NiCr coating at high temperature comparing with the typical mild steel for boiler tube. Results showed that the erosion rate of the mild steel increased with the increase of temperature. The erosion rate of the mild steel at 800°C was 4 times that at 300°C at an erosion angle of 30°. However, the erosion rate of the HVOF sprayed Cr 3 C 2 -NiCr coating was not influenced by the temperature in the range of 300 to 800°C. It is found that the erosion resistance of HVOF sprayed Cr 3 C 2 -NiCr coating was more than 3 time higher than that of the mild steel at 700 to 800°C. In addition to the ploughing on the surface of the worn coating, the cracking along splats interfaces in the coating was clearly observed on the cross-sectional microstructure of the coating. The results indicate that the erosion performance of the HVOF sprayed Cr 3 C 2 -NiCr coating is controlled by the cohesion between splats in the coating and can be further enhanced by improving splat cohesion.

Titanium aluminium based nitride (Ti, Al)N coatings possess excellent tribological behaviour with respect to metal cutting and polymer forming contacts. In the present work TiAlN coatings were deposited by plasma spray process. Three coatings of TiAlN were deposited on AISI-347 grade boiler steel substrate out of which two were thin nano coatings deposited at different temperatures of 500°C and 200°C and one conventional coating was deposited by plasma spraying. The as sprayed coatings were characterized with relative to coating thickness, microhardness, porosity and microstructure. The optical microscopy (OM), the XRD analysis and field mission scanning electron microscope (FESEM with EDAX attachment) techniques have been used to identify various phases formed after coating deposited on the surface of the substrate. Subsequently the sliding wear behaviour of uncoated, PVD sprayed nanostructured thin TiAlN coatings deposited at 500°C and 200°C and plasma sprayed conventional coated AISI-347 grade boiler steel were investigated according to ASTM standard G99-03 using pin on disk wear test rig. Cumulative wear volume loss and coefficient of friction, μ were calculated for the coated as well as uncoated specimens for 10, 15 and 20 N normal loads at a constant sliding velocity of 1 m/sec. The worn out samples were analysed with SEM/EDAX. Wear rates in terms of volumetric loss (mm³/g) for uncoated and coated alloys were compared. The nanostructured TiAlN coatings deposited at 500°C and 200°C has shown minimum wear rate as compared to conventional TiAlN coating and uncoated AISI-347 grade boiler steel. Nanostructured TiAlN coatings were found to be successful in retaining surface contact with the substrate after the wear tests.

In the current work, Ni-20Cr coatings have been developed for potential use in harsh environments of power plant boilers. A pre-synthesized Ni-20Cr nanocrystalline powder was deposited on T22 boiler steel using cold-spray process. The high temperature oxidation behavior of the coating was investigated under cyclic conditions at 900° C for 50 cycles, so as to understand the kinetics of oxidation. Moreover, high temperature erosion-corrosion (E-C) behaviour of the coating was ascertained under cyclic conditions in an actual boiler at 740 ± 10°C for 1500 hours. The oxidized and eroded-corroded samples were characterized using X-ray Diffraction (XRD), Scanning Electron Microscopy/Energy Dispersive Spectroscopy (SEM/EDS) analyses. The microhardness, oxidation and E-C data for the developed coating was compared with an earlier reported cold-spray Ni-20Cr coating, which was developed by using a commercially available micron-sized Ni-20Cr powder. The results showed that the developed coating was found to have 33% high microhardness in comparison with the microstructured Ni-20Cr coating. The oxidation and E-C rates of the steel were found to decrease significantly after the application of the developed coating by 89% and 68% respectively. Moreover the nanostructured coating outperformed the corresponding micro-structured Ni- 20Cr coating with regard to high temperature oxidation and E-C resistance to boiler steel by a significant fraction. The investigated coating was found to have oxidation protective oxides such as Cr 2 O 3 and NiO in its oxide scale and was found to be spallation-free.

In this investigation, a nanostructured NiCr coating was deposited on boiler steel by cold spraying and its oxidation behavior was evaluated under cyclic thermal conditions. Oxidation kinetics were established through weight change measurements and the oxidized samples were characterized using XRD and SEM analysis and X-ray mapping. The nanostructured coating was more than two times harder than its microstructured equivalent and in oxidation tests, reduced the weight gain of the boiler steel by 68%. The coating was found to have protective oxides in its oxide scale and was shown to be spallation-free.

HVOF thermal spray technique was used to deposit Ni-20Cr coating on a ASTM-SA213-T22 boiler steel. The corrosion behaviour was investigated for the uncoated and HVOF spray Ni-20Cr coated boiler steel in a molten salt environment (Na 2 SO 4 -60%V 2 O 5 ) at 900°C for 50 cycles. Each cycle consisted of 1 hour heating in the silicon carbide tube furnace followed by 20 min cooling in air. Mass change technique was used to approximate the kinetics of high temperature corrosion. The uncoated sample suffered intensive spallation along with a significant mass gain as compared to the coated sample. The exposed specimens were characterized by X-ray diffraction [XRD] and scanning electron microscopy/energy dispersive spectroscopy [SEM/EDS]. It was observed that HVOF sprayed Ni-20Cr coating was suitable to provide high temperature corrosion resistance to the given steel in the said(salt) environment.

This study assesses the fireside erosion-corrosion behavior of nanostructured NiCr coatings in a power plant boiler operating at 750 °C. In the experiments, Ni-20Cr nanocrystalline powder was synthesized by ball milling and deposited on T91 boiler steel substrates by HVOF spraying. Coated and uncoated steel specimens were thermally cycled in the superheater zone of a coal fired boiler. After 15 heating and cooling cycles, the specimens were examined and erosion-corrosion kinetics were established via weight-change and thickness-loss measurements. The results show that the nanostructured coatings reduced the erosion-corrosion rate of T91 steel by 85%.

In biomass boilers, corrosion is a prevalent concern that arises at high temperatures. This is mainly because the fuels consumed in these boilers have a high alkali, chlorine, and other molten salt content that has occasionally led to material depletion, leaks, and unforeseen plant shutdowns. Applying protective coatings using thermal spray techniques is a practical answer to this issue. The current work focused on applying powders of Inconel 625 and Inconel 718 to boiler steel using a high-velocity oxy-fuel spraying method. The samples after coating deposition were subjected to the conditions of a biomass-fired boiler for 15 cycles to study the performance of the coatings in a real environment. The decrease of thickness over time was used to evaluate the erosion-corrosion process. Various characterization techniques were used to examine the as-sprayed and eroded-corroded specimens. The X-ray diffraction (XRD) technique was utilized to analyze the phases, while the surface characteristics of powders, coatings, and samples exposed to erosion-corrosion were investigated through scanning electron microscopy (SEM) combined with energy-dispersive X-ray spectroscopy (EDS). When exposed to the actual boiler environment, the findings showed that Inconel 625-coated steel performed better than Inconel 718-coated steel.

In this study, Ni-20Cr alloy powder was synthesized and deposited on T22 boiler steel by HVOF spraying. Coated and uncoated test samples were placed in a silicon carbide tube furnace and subjected to cyclic oxidation conditions in 900 °C air. Oxidation kinetics were established via weight change measurements and oxidation products were characterized based on XRD and SEM-EDS analysis. The results show that in addition to improving the oxidation resistance of the steel, the Ni-20Cr coatings also reduced spallation due to the formation of a protective Cr2O3 phase.

In this study, HVOF sprayed NiCr alloy coatings on A213 TP347H boiler steel are evaluated by severe corrosion tests in a high-temperature molten salt environment. XRD and FE-SEM/EDS analysis results are presented and discussed and correlated with corrosion kinetics.

The goal of this work is to develop a flame sprayed NiCr-Cr 3 C 2 coating that resists oxidation, corrosion, and erosion in boiler environments and to assess the influence of Cr 3 C 2 fraction and sealing on coating performance. In the experiments, NiCr cermet alloys with different proportions of chromium carbide were applied to boiler steel substrates by means of subsonic velocity flame spraying and some of the coatings were sealed with a silicon resin. The paper describes the various tests performed and presents the results. Paper includes a German-language abstract.

In this study, detonation spraying was used to deposit commercially available Ni-20Cr and WC-Co powders on SA213-T22 boiler steel. Coated and uncoated specimens were subjected to 50 thermal cycles in a molten salt boiler environment 900 °C in order to evaluate their hot corrosion behavior. Mass change measurements were made at the end of each cycle to assess corrosion kinetics and XRD and SEM/EDS were used to characterize corrosion products. An analysis of the reaction kinetics and the formation of oxide scales is provided in the paper.

Detonation-gun thermal spray technique was used to deposit commercial available Ni-20Cr and WC-Co coatings on ASTM A213 TP347H boiler steel. The coated specimens were subjected to air environment at 900°C in laboratory furnace to determine high temperature oxidation resistance. Mass change data was recorded to formulate oxidation kinetics of both the coated specimens. The exposed specimens were assessed by field emission scanning electron microscopy and energy dispersive spectroscopy (FE-SEM/EDS) and XRD analysis. The primary focus of the study is attractive oxidation resistance of Detonation gun sprayed Ni-20 Cr coating over the WC-Co coating on the said steel in the air environment.

Nickel-chromium alloys have been used as coatings to deal with oxidation environments at high temperature. The present work is a comparative study of HVOF and cold sprayed Ni-20Cr coating on a boiler steel (SAE 213-T22) in a molten salt environment of Na 2 SO 4 -60%V 2 O 5 at 900°C under cyclic conditions. The weight change technique was used to establish the kinetics of corrosion. X-ray diffraction, surface and cross-sectional FE-SEM/EDS techniques were used to analyse the corrosion products. The hot corrosion resistance of both the coatings was better than the uncoated steel. This may be attributed to the formation of oxides and spinels of nickel and chromium in the coated steels. These oxides might have blocked the pores and splat boundaries, and acted as diffusion barriers to the inward diffusion of corroding species. Based upon the overall results and subsequent analysis of hot-corrosion data the cold spray process may be recommended as a better choice for the deposition of the Ni-20Cr coating on Mo-containing T22 steel in comparison with the HVOF spray process for hot corrosion protection.