Erosion-corrosion is a severe problem observed in the coal fired thermal power plant boilers which lead to premature failure of boiler tubes. Thermal spray coatings have been applied successfully to check the erosion-corrosion of boiler tubes. In the present research work NiCrTiCRe coating powders were successfully deposited on T22 boiler steel by two different coating processes i.e. high velocity oxy-fuel (HVOF) and cold spray process. The performance of the coatings in actual power plant boiler were investigated and compared. The uncoated and coated T22 boiler steels were subjected the superheater zone of the coal fired boiler for a total of 15 consequent cycles. The thickness loss data and weight change analysis were used to establish kinetics of the erosion-corrosion. X-ray diffraction, surface field emission scanning electron microscope/energy dispersive spectroscopy (FE-SEM/EDS) techniques were used in the present work for the analysis. The results of thickness loss data indicated that the cold sprayed coating performed better in thermal power plant boiler environment.