Abstract
In order to overcome the problem of insufficient abradability of existing metal based coatings that cannot meet the requirements of harsh working conditions, this article designs two types of metal based abradable sealing coating materials based on the particle structure of "peeling medium", and studies the basic performance and simulated working condition service performance of the coatings. The research shows that, after undergoing a 1000 hour heat exposure test at high temperature, the two coatings still maintain good hardness, bonding strength, and abradability, indicating that under long-term high-temperature service environment, the two coatings can fracture at the location where the abradable components are exposed, thereby maintaining the abradability and good thermal stability that meet the requirements of use.