Abstract
Recently, laser deposition technologies have made significant advancements in their ability to manufacture high temperature metals and ceramics. One of these technologies, known as Direct Energy Deposition (DED), has the potential to deposit a wide range of materials from polymers to refractory materials, ceramics and functionally graded materials. This study evaluates major microstructural characteristics of WC-Co additively manufactured by DED technology. This material is commonly used for deposition of protective coatings due to its high hardness and excellent wear resistance. To this end, hardness and wear resistance of the DED processed samples were also investigated in this study. WC-Co coatings are generally deposited using various thermal spray technologies. However, it is speculated that DED deposited WC-Co could provide superior properties such as higher hardness and wear resistance. A DED manufactured WC-Co sample was examined by Optical Microscopy (OM), Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), and X-ray Diffraction (XRD). Those studies could provide information about important microstructural features, chemical compositions and phase distribution. All the tests were also repeated on High-Velocity Oxygen Fuel (HVOF) deposited WC-Co with the same composition. Both DED and HVOF produced WC-Co coatings experience decomposition of the carbides into compound phases; however, the DED deposited sample displays unique dendritic and eutectic structures that improve the hardness and wear properties compared to the homogenous HVOF coating. In addition, DED produced samples show higher hardness and relatively better wear resistance compared to the HVOF deposited ones. The obtained results could establish a relationship between microstructural characteristics with hardness and wear properties of both samples.