Atmospheric plasma sprayed (APS) CuNiIn coatings have been widely used for fretting wear protection in many important areas such as aircraft engines for decades. The oxides in CuNiIn coating prepared by APS hinder splat bonding formation and thus degrade the coating fretting performance. In this study, CuNiIn powders of different boron contents were designed to realize the self-oxide-cleaning effect for in-flight molten droplets and thus deposit the dense CuNiIn coating with high fretting performance. Scanning electron microscope was used to characterize the microstructure. The oxygen content in the coating was measured by the inert gas fusion technique. Fretting test was performed for three coatings under different loadings. The results show that CuNiIn2B and CuNiIn4B coatings presented the oxide content of 0.40wt% and 0.38wt%, which are lower than 1.6wt% of the CuNiIn coating. The oxygen content in the CuNiIn4B coating decreased with the increase of spray distance while the oxygen content in CuNiIn coating increased with the increase of the spray distance. Such results clearly reveal the boron in-situ deoxidizing effect of inflight molten droplets. As a result, the dense CuNiIn2B and CuNiIn4B coatings were deposited with oxide-free molten droplets. The test results showed that the fretting wear performance of B-alloyed CuNiIn coatings were increased by a factor over three comparing with conventional CuNiIn coating.

This content is only available as a PDF.
You do not currently have access to this content.