Abstract
Material’s tensile strength can be improved by the presence of a body-centered cubic (BCC) phase, which is essential in highstrength applications and highly corrosive environments. Thus, synthesizing a BCC single-phase, equiatomic AlCoCrFeNi high-entropy alloy (HEA) feedstock particle using a highenergy mechanical alloying (HE-MA) method was investigated. The transient alloy particles were developed using a planetary mill at a constant rotational speed of 580 rpm employing milling times in the range of 4 to 24 hours. During the process, stearic acid of 3 wt.% of the precursor composition was used as a process-controlling agent (PCA). Two HE-MA manufacturing regimes were utilized: i) conventional (milling constituent elements simultaneously), and ii) sequential (progressive milling while adding elements in a certain order). In addition to the conventional method, a sequential regime was employed to develop FeNiCoCrAl, wherein individual elements were added every 4 hours to the starting/milled Fe + Ni mixture. Based on the results, the HE-MA FeNiCoCrAl showed a BCC single-phase formation after 24 hours, with no intermetallic or contamination traceability. Finally, a nanoindentation hardness measurement was carried out to support the observed phase transformation before and after the HE-MA process.