Abstract
The influence of air plasma sprayed alumina coating geometry, microstructure, interface roughness on its delamination and crack propagation resistance during low temperature thermal cycling, i.e. thermal mismatch stress, is investigated both numerically and experimentally. Previous studies on thermal cycling loading concentrate on flat, numerically designed locally curved specimens and/or mathematically modeled roughness without extension towards real coating morphology, which renders the conclusions less practically driven. Results show that arbitrarily oriented cracks originate predominantly near the coating/substrate interface and propagate along zones of high tensile and shear residual stress. The crack path deflection was attributed to the complex stress concentration structure resultant from the intricate microstructural porosity and coating general convex geometry. Microstructural features such as porosity increase the interfacial and coating tensile stress, which may lead to important delamination processes even during low temperature thermal cycling.