Abstract
This work investigates the sliding wear resistance of alumina coatings deposited on stainless steel substrates by HVOF and air plasma spraying, using fine (1-5 μm) and conventional (10-45 μm) powders. Sliding wear tests were carried out using a sintered WC-Co ball as the counter-body and the wear tracks were examined to obtain a better understanding of wear mechanisms. HVOF coatings showed an order of magnitude improvement in wear resistance compared to their APS counterparts. The disparity in wear performance is correlated to differences in phase composition, porosity, hardness, and fracture toughness as revealed by SEM and XRD analysis and nanoindentation testing. The development of tribofilms and their role in wear behavior is also discussed.