In this investigation, an air plasma sprayed TBC system consisting of a CoNiCrAlY bond coat (BC) and a YSZ topcoat (TC) is produced with a PVD AlOx interlayer in order to study its effect on thermally grown oxides. For comparative purposes, a reference TBC without the AlOx interlayer was also prepared and studied. A cyclic thermal load was applied to both systems and the coatings were examined after 6, 12, 24, 40, and 80 cycles. Crack lengths were measured in the YSZ layer and TGO thicknesses were assessed at the BC-TC interface. An examination of coating microstructures revealed the expected mixed-mode failure in both TBCs. In comparison to the reference TBC, the system with the AlOx interlayer showed reduced crack formation in the TC and slowed TGO formation at the BC-TC interface both during and after thermal treatment.