Improving Corrosion Resistance of Al6061 Coating Deposited by an In-Situ Shot-Peening Assisted Cold Spray

This study demonstrates a novel method for improving the corrosion resistance of cold sprayed Al6061 coatings. Large stainless steel particles were added to a commercial Al6061 powder and the mixture was deposited on Mg alloy AZ31B substrates using nitrogen gas at low working pressure and temperature. It is shown that the stainless steel particles had a shot-peening effect, thus increasing the density as well as the corrosion resistance of Al6061 coatings. SEM examination showed that no stainless steel particles were incorporated in the coating.