The Effect of Severe Shot Peening as Pre/Post Treatment on Fatigue Behavior of Cold Spray Coating

This study evaluates the influence of shot peening on the fatigue life of cold spray aluminum alloy 6082 coatings. A pneumatic blast machine with standard steel shot was used to peen both uncoated and coated substrates. Six test groups representing different treatment protocols were characterized in terms of residual stress, roughness, and rotating bending fatigue. The results show that the best fatigue performance is obtained by intense shot peening prior to cold spraying. Post-treatment shot peening, in contrast, had a detrimental effect as a large portion of the kinetic energy is absorbed in the coating, resulting in surface damage rather than further work hardening.