Abstract
A magnesium coating with a low porosity and high microhardness was elaborated using cold spraying. However at present, a poor bonding strength between the coating and substrate limits its application. This paper aims at improving the bonding strength between the coating and substrate using substrate preheating. Aluminum substrates were heated to 100, 200 and 300°C respectively by a flame prior to cold spraying. The results show that substrate preheating can significantly increase the bonding strength. The bonding strength increased from 3.3±0.8 MPa to 11.6±0.5 MPa when the substrate temperature increased from room-temperature to 200°C. The fracture analyses show that the coating fracture occurred within the coating when the substrate was preheated at 200°C.