Molybdenum silicides have the potential as protective coatings for high-temperature applications because of their high melting point and their high-temperature oxidation resistance. Reinforcing MoSi2 with SiC shows an improvement of its low toughness at room temperature and low creep resistance at temperatures above the brittle-ductile transition temperature of approximately 700-1000 °C. A new kind of powder processing was used to produce MoSi2 and MoSi2-SiC as a feedstock for thermal spraying. Mixtures of the elemental powders, molybdenum and silicon, were prepared by milling and subsequent heat treatment to get highly dispersed, pre-reacted powders. As high-energy milling equipment, a planetary ball mill was used to prepare the powders. In the case of reinforcement, SiC was mixed to the pre-reacted MoSi2 at the end of the milling process, that means before heat treatment. On these as-milled powders, X-ray diffraction characterization (XRD), scanning electron microscopy (SEM), electron probe micro analysis (EPMA) and determination of the oxygen level were carried out. Vacuum plasma spraying has been used to deposit the powders onto a carbon steel substrate. Evaluated coating characteristics were the microstructure (SEM), phases (XRD), EPMA, oxygen content, microhardness and surface roughness. Tests at high temperatures will be considered in future work.