Methodology to evaluate the adhesive strength between the MCrAlY alloy coating film and the Ni-base superalloy substrate was studied and proposed. By employing the double cantilever beam specimens which were taken from the CoNiCrAlY alloy coated Ni-base superalloy, the fatigue crack propagation tests along the interface were carried out. Through the work particular attention was given to the threshold level to the fatigue crack propagation along the interface as a measure to represent the adhesive strength, based on fracture mechanics approach. The effects of temperature, the surface finishing of the substrate and the long term thermal aging on the adhesive strength were also investigated.