In this paper, the Young's modulus, Poisson's ratio, and ultimate tensile strength of HVOF-sprayed NiCr (80/20) coating are evaluated by a uniaxial tensile test parallel to the coating plane. The effect of stand off distance is also considered. It is observed that, in the tensile test, the alloy NiCr (80/20) showed moduli of elasticity between 130 and 155 GPa and tensile strengths between 185 and 210 MPa. For the WC-CoCr alloy, the modulus of elasticity was between 185 and 210 MPa and the tensile strength was around 80 MPa. Paper includes a German-language abstract.