This study aims to develop a metal-based compatibilizing sublayer on a Carbon Fiber-Reinforced Polymer (CFRP) composite to overcome the erosion issue of polymer substrate using the cold spray deposition technique. The objective is to contribute to the in-situ repair of aircraft structures. Two cases of sublayers, i.e., Al-based sublayer (1126 μm thick) and Cu-based sublayer (547 μm thick), have been prepared and co-cured with the CFRP substrates by pressure assisted molding process. Gas-atomized copper powders were deposited on a reference sample of aluminum panel (A-0) and on two functionalized composite substrates (A-1 and C-1) by a high-pressure cold spraying (HPCS) process. The results show that cold spray deposition onto the Al-based sublayer leads to a coating formation whereas the Cu-based sublayer is strongly eroded by the supersonic collision of copper powders. Scanning electronic microscope (SEM) morphologies were used to investigate the HPCS deposition mechanisms on various configurations of substrates. It was found that the high deposition efficiency of case Cu/A-0 was achieved by metallic bonding, evidenced by the significant flattening powders and agglomeration phenomenon of multiple particles. The copper particles of case Cu/A-1, encapsulated by the deformed aluminum powders, could anchor to the substrate via mechanical interlocking, whereas only pure localized fracture of epoxy and exposed broken carbon fibers were observed on the substrate of case Cu/C-1. The results demonstrated the feasibility of an Al-based sublayer-assisted cold spray process for the thermosetting CFRP composite to achieve a successful deposition of copper powders, which also emphasized the necessity to search an optimal material coupling between sublayers and coatings.