Fracture Toughness of Cold Sprayed Pure Metals

The fracture toughness of pure Al, Cu, Ni, and Ti deposited by cold spraying was investigated to gain a better understanding of the damage process and quantify material performance. Rectangular specimens of self-standing deposits with fatigue pre-cracks were tested in three-point bending. KIC values were obtained from J-R curves and stress-strain curves were plotted. The cold-sprayed deposits exhibited significantly lower fracture toughness than the same wrought materials, and fractographic analysis revealed either ductile or cleavage intergranular fracture as the major failure mode.