High-Temperature Corrosion Behavior of Selected Thermally Sprayed Alloy-Based Coatings in an Aggressive Environment at 690°C

This study evaluates the hot corrosion behavior of NiCoCrAlY, NiCoCrAlYHfSi, NiCoCrAlTaReY, and CoCrAlYTaCSi coatings on 1.4923 stainless steel, applied by high-pressure HVOF spraying. All coatings were cycled in in an environment of Na₂SO₄ and 82% Fe₂(SO₄)₃ at 690 °C. Each cycle consisted of 1 h of heating in a silicon carbide tube furnace followed by 20 min of cooling. Weight change measurements were performed after each cycle to track corrosion kinetics, and SEM and EDS analysis were employed to analyze the corrosion mechanism. CoCrAlYTaCSi showed the best corrosion resistance of the coatings tested.