Corrosion Protection of a 5xxx Series Aluminum Alloy by Cold Spray Process

In this investigation, 5083 aluminum alloy coatings were deposited on substrates of the same material by high-pressure cold spraying. Spray trials were carried out using powders with size ranges of 5-20 µm and 20-44 µm, gas temperatures of 673 K and 773 K, and nitrogen and helium process gases. Coatings and coating-substrate interfaces were evaluated primarily by SEM and EDS, while XRD was used to examine coating stresses and oxidation effects. Corrosion protection was assessed by electrochemical potentiodynamic measurements in synthetic seawater and Knoop indentations tests were conducted as a measure of work-hardening and mechanical integrity of the coatings. Test results are presented and correlated with spray parameters.