Abstract
It was possible to fabricate cubic-AlN (c-AlN) based coating through the reaction between Al powder and the N2/H2 plasma in APS system. The fabricated coating was about 100 μm with hardness about 540 Hv, which is much higher than the hardness of Al. The formation of the cubic phase in APS is directly related to the rapid solidification phenomena of plasma spraying process. The sprayed powder particles show rapid cooling rates upon impact with the substrate, which prevent its complete crystal growth. The nitride content increased with the spray distance due to increase the flight time of Al particles in the N2 plasma. Using smaller particle size improved the nitriding reaction at short spray distance due to increasing the particle temperature. However increasing the particle temperature leads to excessive vaporization of Al particles and completing nitriding reaction during flight, therefore suppressing the coatings thickness. The nitriding reaction of the larger particle size Al powders can be enhanced through NH4Cl powders addition. That NH4Cl addition changed the reaction pass way from liquid-gas to vapor-phase intermediate mechanism.