Effects of Gas Temperature, Gas Pressure, and Particle Characteristics on Cold Sprayed Pure Titanium Coatings

This work investigates the influence of nitrogen gas pressure and temperature on the structure and properties of cold sprayed titanium coatings. Two guns were used to assess the effect of impinging particle temperature. Particle speed was measured and used to calculate critical velocity for selected experimental conditions. The results show that increasing the temperature and pressure of the gas propellant reduces coating porosity and increases hardness, flattening ratio, and deposition efficiency. At the maximum pressure and temperature (40 bar and 800 °C) for nitrogen gas, coating density was close to the value reported for cold sprayed titanium produced using helium as the propellant.