Abstract
Ductile iron pipes (DIP) have been used worldwide since 1960s for water transmission and distribution mains. By 1979, ductile iron pipe largely replaced cast iron as the predominant material in water industry. Zn and Zn/Al 85/15 coatings applied by thermal spray technique are used for the protection of the ductile iron pipe against corrosion in heterogeneous soil conditions. In this study, heat treated and non-heat treated ductile iron pipe samples were coated with Zn and Zn/Al 85/15 in optimum spray parameters by twin wire electric arc (TWEA) spraying technique. The coatings were investigated by optical microscopy, scanning electron microscopy (SEM), and analyzed by energy dispersive spectrometer (EDS). Both Zn and Zn/Al 85/15 coatings showed fairly good lamellar structure with acceptable amount of internal porosities and oxides. Annealing oxides available on pipe surface helped the bonding of coatings. The protection performance of the coatings was compared with accelerated corrosion (salt spray) test according to the ASTM B 117 and corrosion products were analyzed by SEM and EDS technique. Salt spray test results showed that Zn/Al 85/15 coatings have better corrosion resistance than Zn coatings and annealing oxide on ductile iron pipe acts as a good corrosion resistant protective layer.