Abstract
The goal of this paper is to evaluate high temperature ageing properties of a new high temperature titanium blade compatible abradable material DurabradeTM 2614. Coatings were tested in as-sprayed condition and after ageing at 550°C and 655°C for up to 8,030 hours. Coating properties such as coating hardness, erosion resistance, and cohesive strength were evaluated at regular time intervals. Abradability was tested in as-sprayed condition and after ageing. The results show that coating hardness, GE erosion resistance, and cohesive strength of the new material change most in the first 200 hours and SMC90 erosion resistance, and oxidation weight gain change most in the first 1,000 hours and then they stabilize at values that guarantee good seal performance. The good performance of the new seal after 8,030 hours ageing has been demonstrated by abradability and erosion testing.